Comparison of the Efficiency of Inorganic Nonmetal Pigments with Zinc Powder in Anticorrosion Paints
Year: 2006
Type of publication: článek v odborném periodiku
Name of source: Progress in Organic Coatings
Publisher name: Elsevier Science BV
Place: Amsterdam
Page from-to: 1-10
Titles:
Language Name Abstract Keywords
cze Porovnání antikorozní účinnosti kovového zinku s inhibičními antikorozními pigmenty v nátěrech Práce se zabývá studiem účinnosti různých antikorozních pigmentů z hlediska jejich chemického složení. Byly připraveny dvě řady nátěrů, které obsahovaly antikorozní pigment v koncentraci PVC = 10% a druhá řada ve které PVC = CPVC antikorozního pigmentu. Byly použity následující netoxické antikorozní pigmenty: fosforečnan zinečnatý, fosfomolybdenan zinečnatý, hydrogenfosforečnan vápenatý, fosforečnan zinečnatý modifikovaný organickým inhibitorem koroze, polyfosfosilikát strontnato ? hlinitý, polyfosforečnan zinečnato ? hlinitý, metaboritan vápenatý, ferit vápenatý, borokřemičitan vápenatý. Pro porovnání antikorozní účinnosti byl použit chroman strontnatý. Vyhodnocení antikorozní účinnosti bylo provedeno porovnáním s antikorozní účinností kovového zinku. U připravených epoxyesterových základních nátěrů byl sledován vliv typu pigmentu na antikorozní vlastnosti filmů. Antikorozní účinnost byla získána z testů v kondenzační komoře, solné komoře a z testu chemické odolnosti pigmentovaných nátěrů. antikorozní pigmenty, epoxyesterový nátěr, zinkový prach, fosfáty, ferity, křemičitany, chromany, korozní testy
eng Comparison of the Efficiency of Inorganic Nonmetal Pigments with Zinc Powder in Anticorrosion Paints This paper deals with the study of properties of anticorrosion pigments of varying chemical composition in epoxyester paints. Two type lines of paints were prepared. The first line comprised an anticorrosion pigment with a PVC concentration of 10% while the other line comprised an anticorrosion pigment with a PVC concentration = CPVC. The following nontoxic anticorrosion pigments were observed: zinc phosphate, zinc phosphomolybdate, calcium hydrogen phosphate, zinc phosphate modified with an organic corrosion inhibitor, strontium-aluminum polyphosphosilicate, zinc-aluminum polyphosphate, calcium metaborate, calcium ferrite, calcium borosoliciate, and strontium chromate. The prepared epoxyester primers were observed for the effect of the type of pigment on the anticorrosion properties of paint coatings. Anticorrosion efficiency was derived from tests in a condenser chamber and in a salt spray cabinet as well as from a test of chemical resistance of pigmented coatings. The evaluation of anticorrosion efficiency of inorganic nonmetal pigments was carried out by means of comparison with anticorrosion efficiency of metal dust. Keywords: anticorrosion pigments, epoxyester coatings, zinc dust, phosphates, ferrites, silicates, chromates, corrosion tests. anticorrosion pigments, epoxyester coatings, zinc dust, phosphates, ferrites, silicates, chromates, corrosion tests

Departments

Other Parts

Map

en.mapy.cz

Services

Popular Links

© 2023 University of Pardubice, Studentská 95, 532 10 Pardubice 2
Phone: +420 466 036 111, 466 036 112, 466 036 113
Webmaster, RSS
Data box ID: f5vj9hu
Accessibility Statement
CC BY-NC-ND 4.0Creative CommonsAttributionNonCommercialNoDerivatives