Dynamic colour and appearance of thermochromic offset inks
Authors: Kulčar Rahela | Panák Ondrej | Otáhalová Lenka | Friškovec Mojca | Kaplanová Marie | Klanjšek Gunde Marta
Year: 2010
Type of publication: ostatní - článek ve sborníku
Name of source: Proceedings of 5th International Symposium on Novelties in Graphics
Publisher name: Univerza v Ljubljani
Place: Ljublana
Page from-to: 795-800
Titles:
Language Name Abstract Keywords
cze Dynamický vzhled termochromních ofsetových barev Pro měření byl použit přístroj Krüss DSA 100 včetně originálního softwaru a databáze parametrů testovacích kapalin. Pro výpočet volné povrchové energie byly použity metody Owens-Wendta (geometrický průměr), Wu (harmonický průměr) a tzv. acido-bazická teorie navržená van Ossem, Chaudhurym a Goodem na základě modelu Lewise. Použitím těchto rovnic získáme hodnoty pro celkovou disperzní a polární část volné povrchové energie pryžových potahů. První zkušenost s měřením tohoto typu vzorků s drsným a heterogenním povrchem a výpočty pomocí těchto modelů vedla k značně rozdílným výsledkům. termochromní barva; kolorimetrie; hystereze; lesk
eng Dynamic colour and appearance of thermochromic offset inks The offset inks with activation temperature of 31 °C in black, red and magenta colour shades were applied. The size of the largest pigment particles was measured by fitness-of-grind gage. It is approximately 2,5 m for the three studied inks. Three paper substrates were applied, gloss coated (250 g/m2, PPS roughness 1,31 m), matt (250 g/m2, PPS roughness 1,56 m) and label (80 g/m2, PPS roughness 1,68 m). The samples were printed by IGT Printability Tester C1 with printing speed of 0,3 m/s and different printing force. Wet thickness was expressed in weight per square meter of substrate whereas dry layer thickness was measured by optical profilometer. The specular gloss at grazing incidence angle 85° was measured as a function of layer thickness. Different thickness behaviour was obtained for the black ink and very similar for the red and magenta. Such results might show some differences in particle size distribution. thermochromic ink; colorimetry; hysteresis; gloss

Departments

Other Parts

Map

en.mapy.cz

Services

Popular Links

© 2023 University of Pardubice, Studentská 95, 532 10 Pardubice 2
Phone: +420 466 036 111, 466 036 112, 466 036 113
Webmaster, RSS
Data box ID: f5vj9hu
Accessibility Statement
CC BY-NC-ND 4.0Creative CommonsAttributionNonCommercialNoDerivatives