Structural study of PbO-MoO3-P2O5 glasses by Raman and NMR spectroscopy
Authors: Koudelka Ladislav | Rösslerová Ivana | Holubová Jana | Mošner Petr | Montagne Lionel | Revel Bertrand
Year: 2011
Type of publication: článek v odborném periodiku
Name of source: Journal of Non-Crystalline Solids
Publisher name: Elsevier Science BV
Place: Amsterdam
Page from-to: 2816-2821
Titles:
Language Name Abstract Keywords
cze Studium struktury skel PbO-MoO3-P2O5 Ramanovou a NMR spektroskopií Skla ternárního systému PbO–MoO3–P2O5 byla syntetizována ve třech kompozičních řadách 100−x)[0.5PbO–0.5P2O5]–xMoO3 (A), 50PbO–yMoO3–(50−y)P2O5 (B) a (50−z)PbO–xMoO3–50P2O5 (C) a jejich struktura byla studována Ramanovou a 31P NMR spektroskopií. V řadě(100−x)[0.5PbO–0.5P2O5]–xMoO3 homogenní skla byla připravena s obsahem 0–70 mol% MoO3. 31P MAS NMR spektra ukázala, že v řadě (A)přídavky MoO3 mají za následek zkracování fosfátových řetězců a transformaci Q2 celků Q1 a Q0 celky, které dominují ve sklech s vysokým obsahem MoO3. Oktaedrické strukturní celky MoO6 dominují ve většině skel a vyskytují se též ve struktuře krystalické sloučeniny Pb(MoO2)2(PO4)2, která má stejné složení jako sklo 50Pb(PO3)2–50MoO3. Analysa Ramananových spekter skel řady (B)s vysokým obsahem MoO3 ukázala na transformaci oktaešdrických celků MoO6 na tetraedrické celky MoO4. fosfáty;sklo;struktura;Ramanova spektra;NMR spektra
eng Structural study of PbO-MoO3-P2O5 glasses by Raman and NMR spectroscopy Glasses in the ternary system PbO–MoO3–P2O5 were prepared in three compositional series (100−x)[0.5PbO–0.5P2O5]–xMoO3 (A), 50PbO–yMoO3–(50−y)P2O5 (B) and (50−z)PbO–xMoO3–50P2O5 (C) and their structure was studied by Raman and 31P NMR spectroscopies. In the compositional series (100−x) [0.5PbO–0.5P2O5]–xMoO3 homogeneous glasses were prepared in the concentration region of 0–70 mol% MoO3. 31P MAS NMR spectra reveal that in the glass series (A) the incorporation of MoO3 results in the shortening of phosphate chains and gradual transformation Q2 units into Q2 and Q0 units, prevailing in glasses with a high MoO3 content. Octahedral structural units MoO6 dominate in most glass compositions and they are present also in the structure of Pb(MoO2)2(PO4)2 compound corresponding to the glass composition 50Pb(PO3)2–50MoO3. The analysis of Raman spectra of glasses of the (B) series with a high MoO3 content showed the transformation of octahedral MoO6 units into tetrahedral MoO4 units. Phosphate;Glass;Structure;Raman;NMR

Departments

Other Parts

Map

en.mapy.cz

Services

Popular Links

© 2023 University of Pardubice, Studentská 95, 532 10 Pardubice 2
Phone: +420 466 036 111, 466 036 112, 466 036 113
Webmaster, RSS
Data box ID: f5vj9hu
Accessibility Statement
CC BY-NC-ND 4.0Creative CommonsAttributionNonCommercialNoDerivatives