Thermal properties and crystallization of PbO–MoO3–P2O5 glasses

Authors: Rösslerová Ivana | Koudelka Ladislav | Černošek Zdeněk | Mošner Petr | Beneš Ludvík

Year: 2011

Type of publication: článek v odborném periodiku

Name of source: Journal of Materials Science

Publisher name: Springer

Page from-to: 6751-6757

Titles:

Language	Name	Abstract	Keywords
cze	Termické vlastnosti a krystalizace skel PbO–MoO3–P2O5	Termické vlastnosti a krystalizace vbyly studovány u skel ternárního systímu PbO–MoO3–P2O5 ve třech kompozičních řadách (100-x)[0.5PbO–0.5P2O5]–xMoO3 (A), 50PbO–yMoO3–(50-y)P2O5 (B), a (50-z)PbO–zMoO3–50P2O5 (C). U studovaných skel byly stanoveny hodnoty teploty skelné transformace, teploty krystalizace, koeficient teplotní roztažnosti a dilatční teplota měknutí pmocí DTA a dilatometie. Produkty krystalizace skelných vzorků byly studovány pocí RTG difrakce a Ramanovy spektroscopie. RTG difrakce zjistila přítomnost fází PbP2O6, Pb3P4O13, a PbMoO4 u vzorků řady B. Ve vzorcích s vysokým obsahem MoO3 byly identifikovány sloučeniny Pb(MoO2)2(PO4)2 u řady A a (MoO2)(PO3)2 u řady C. Ramanova spektra potvrdila výsledky RTG analýzy a poskytla též informace o tepelné stabilitě některých skel a tvrobě skelně-krystalických fází.	sklo;termická analýza;krystalizace;RTG difrakce;Ramanova spektra
eng	Thermal properties and crystallization of PbO–MoO3–P2O5 glasses	Thermal properties and crystallization of glasses from PbO–MoO3–P2O5 ternary system were studied in three compositional series (100-x)[0.5PbO–0.5P2O5]–xMoO3 (A), 50PbO–yMoO3–(50-y)P2O5 (B), and (50-z)PbO–zMoO3–50P2O5 (C). Glass transition temperature, crystallization temperature, coefficient of thermal expansion,and dilatation softening temperature of the studied glasses were determined by differential thermal analysis and dilatometry. Crystallization products of annealed glass samples were investigated by X-ray diffraction and Raman spectroscopy. XRD of crystallized glasses revealed the formation of PbP2O6, Pb3P4O13, and PbMoO4 in the samples of the B series. In the series A and C in the samples with a high MoO3 content, crystalline compounds of Pb(MoO2)2(PO4)2 and (MoO2)(PO3)2, respectively, were identified. Raman spectra confirmed the results of XRD and provided also information on thermal stability of glasses and formation of glass-crystalline phases. in the studied glass series.	glass;thermal analysis;crystallization;Raman;XRD