High-pressure vibrational and optical study of Bi2Te3
Authors: Vilaplana R. | Gomis O. | Manjón F. J. | Segura A. | Pérez-González E. | Rodríguez-Hernández P. | Munoz A. | González J. | Marín-Borrás V. | Munoz-Sanjose V. | Drašar Čestmír | Kucek Vladimír
Year: 2011
Type of publication: článek v odborném periodiku
Name of source: Physical Review B
Publisher name: American Physical Society
Place: College Park
Page from-to: "104112-1"-"104112-13"
Titles:
Language Name Abstract Keywords
cze Studium vibračních a optických vlastností Bi2Te3 za vysokých tlaků Článek popisuje experimentální a teoretické studium mřížkových vibračních módů do 23 GPa a optických vlastností (reflexe a absorbce) do 10 GPa. Nepřímý gap fáze za nízkých tlaků se snižuje se zvyšujícím se tlakem. Ramanovské aktivní módy byly sledovány do 7.4 GPa. Byly studovány fázové přechody se zvyšujícím se tlakem. Po uvolňení tlaku se Bi2Te3 vrací zpět do původní rhomoedrální fáze po případné hysterezi. Byly studovány a diskutovány Ramanovské a IČ módové symetrie, frekvence a jejich závislost na tlaku v různých fázích. Bi2Te3;vysoké tlaky;Ramanova spektroskopie;infračervená spektroskopie
eng High-pressure vibrational and optical study of Bi2Te3 We report an experimental and theoretical lattice dynamics study of bismuth telluride (Bi2Te3) up to 23 GPa together with an experimental and theoretical study of the optical absorption and reflection up to 10 GPa. The indirect bandgap of the low-pressure (R-3m) phase (α-Bi2Te3) was observed to decrease with pressure. In regard to lattice dynamics, Raman-active modes of α-Bi2Te3 were observed up to 7.4 GPa. The pressure dependence of their frequency and width provides evidence of the presence of an transition around 4.0 GPa. On further increasing pressure two additional phase transitions have been observed near 15.5 and 21.6 GPa in good agreement with the structures recently observed by means of x-ray diffraction at high pressures in Bi2Te3. After release of pressure the sample reverts back to the original rhombohedral phase after considerable hysteresis. Raman- and IR-mode symmetries, frequencies, and pressure coefficients in the different phases are reported and discussed. Bi2Te3;high pressure;Raman spectroscopy;infrared spectroscopy

Departments

Other Parts

Map

en.mapy.cz

Services

Popular Links

© 2023 University of Pardubice, Studentská 95, 532 10 Pardubice 2
Phone: +420 466 036 111, 466 036 112, 466 036 113
Webmaster, RSS
Data box ID: f5vj9hu
Accessibility Statement
CC BY-NC-ND 4.0Creative CommonsAttributionNonCommercialNoDerivatives