STRUKTURA A VLASTNOSTI BOROFOSFÁTOVÝCH SKEL OLOVNATÝCH DOTOVANÝCH OXIDEM MOLYBDENOVÝM
Authors: Rösslerová Ivana | Koudelka Ladislav | Vlček Miroslav
Year: 2011
Type of publication: článek ve sborníku
Name of source: Zborník príspevkov, zvláštní číslo časopisu Sklář a keramik, ročník 61 (2011)
Publisher name: Česká sklářská společnost
Place: Teplice
Page from-to: 129-133
Titles:
Language Name Abstract Keywords
cze STRUKTURA A VLASTNOSTI BOROFOSFÁTOVÝCH SKEL OLOVNATÝCH DOTOVANÝCH OXIDEM MOLYBDENOVÝM Borofosfátová skla olovnatá modifikovaná oxidem molybdenovým s různým poéměrem B2O3/P2O5 byla připravena a studována v kompozičních řadách 1-x)[50PbO-10B2O3-40P2O5]-xMoO3 s obsahem 0-70 mol% MoO3 and v řadách 1-x)[50PbO-yB2O3-(50-y)P2O5]-xMoO3 s poměrem B2O3/P2O5 5/45, 10/40 a 15/35 a obsahem MoO3 rovým 0, 20, 40 and 60 mol%. 31P MAS NMR spektra ukázala na depolymerizaci fosfátových řetězců vestavováním molybdátových celků. 11B MAS NMR spectra ukázala na tvorbu směsných strukturních celků s vazbami B-O-Mo - B(OP)3(OMo) a B(OP)2(OMo)2, jejichž počet roste s růstem obsahu MoO3, stejně tak jako počet trigonálních strkturních celků BO3. Ramanova spektra ukázala na tvorbu molybdátových klastrů z oktaedrických celků MoO6 propojených vazbami Mo-O-Mo. skla;NMR;Ramanova spektra;struktura;vlastnosti
eng Structure and properties of lead borophosphate glasses modified by molybdenum oxide Lead borophosphate glasses doped with MoO3 with different ratio of B2O3/P2O5 were prepared. Glasses were studied in the dependence on the MoO3 content in compositional series (1-x)[50PbO-10B2O3-40P2O5]-xMoO3 in the range of 0-70 mol% MoO3 and in the compositional series (1-x)[50PbO-yB2O3-(50-y)P2O5]-xMoO3 with the B2O3/P2O5 ratio equal to 5/45, 10/40 and 15/35 at the MoO3 content 0, 20, 40 and 60 mol%. 31P MAS NMR spectra showed on the depolymerization of phosphate network by the incorporation of molybdate structural units. 11B MAS NMR spectra revealed the formation of mixed structural units with B-O-Mo bonds - B(OP)3(OMo) and B(OP)2(OMo)2, the content of which increases with increasing MoO3 content as well as the number of trigonal BO3 units. Raman spectra revealed formation of molybdate clusters formed by MoO6 octahedra interconnected by Mo-O-Mo bonds. glasses;NMR;Raman;structure;properties

Departments

Other Parts

Map

en.mapy.cz

Services

Popular Links

© 2023 University of Pardubice, Studentská 95, 532 10 Pardubice 2
Phone: +420 466 036 111, 466 036 112, 466 036 113
Webmaster, RSS
Data box ID: f5vj9hu
Accessibility Statement
CC BY-NC-ND 4.0Creative CommonsAttributionNonCommercialNoDerivatives