Advanced Plastic Explosive Based on BCHMX Compared with Composition C4 and Semtex 10
Authors: Elbeih Ahmed Ikhlas Mohamed | Pachmáň Jiří | Trzcinski Waldemar | Zeman Svatopluk | Akštein Zbyněk
Year: 2011
Type of publication: článek ve sborníku
Name of source: Proceedings of the 14th Seminar New Trends of Research of Energetic Materials
Publisher name: Univerzita Pardubice
Place: Pardubice
Page from-to: 120-127
Titles:
Language Name Abstract Keywords
cze Zdokonalená plastická trhavina na bázi BCHMX v porovnání s Composition C4 a Semtexem 10 BCHMX byl studován jako komponenta plastické trhaviny se silikonovou matricí. Pro srovnání byla použita původní trhavina C4 s náplní RDX a také Semtex 10 s náplní PETN. Čistá výbušniny jako aktivní náplně plastických trhavin byly studovány také.. Byly měřeny citlivost k nárazu a tření. Tepelná stabilita byla studována pomocí Diferenční termická analýza (DTA) a výstupy byly vyhodnoceny Kissingerovou metodou. Detonační rychlost byla měřena experimentálně a ostatní detonační parametryi byly vypočteny pomocí CHEETAH kódu. Na základě vzájemného porovnání získaných výsledků byl učiněn závěr, že nové formulace má nižší citlivost k nárazu a tření než složení C4 a Semtex 10; má také vyšší tepelnou stabilitu. Detonační tlak a výbuchévá energie nové formulace byla vyšší než původních plastických trhavin, zatímco její měřené detonační rychlost byly na stejné úrovni jako u složení C4 plastické trhaviny; BCHMX; Composition C4; silokon
eng Advanced Plastic Explosive Based on BCHMX Compared with Composition C4 and Semtex 10 BCHMX was studied as a plastic explosive bonded by Silicone matrix. For comparison the original plastic explosives, Composition C4 based on RDX and Semtex 10 based on PETN were studied. Pure explosives used as active material in the plastic compositions were included as well. Sensitivity to impact and friction were measured. The thermal stability was studied using differential thermal analysis (DTA) and the outputs were evaluated by Kissinger method. The detonation velocity was measured experimentally and the detonation characteristics were calculated by means of CHEETAH code. On the basis of mutual comparison of all the obtained results, it was concluded that the new formulation has lower sensitivity to impact and friction than Composition C4 and Semtex 10; also it has higher thermal stability. Detonation pressure and detonation energy of the new formulation were higher than the original plastic explosives used while its measured detonation velocity were at the same level of Composition C4 plastic explosives; BCHMX; composition C4; Semtex 10; silicone

Departments

Other Parts

Map

en.mapy.cz

Services

Popular Links

© 2023 University of Pardubice, Studentská 95, 532 10 Pardubice 2
Phone: +420 466 036 111, 466 036 112, 466 036 113
Webmaster, RSS
Data box ID: f5vj9hu
Accessibility Statement
CC BY-NC-ND 4.0Creative CommonsAttributionNonCommercialNoDerivatives