Investigation of mechanical resistance and corrosion-inhibition properties of surface-modified fillers with polyaniline in organic coatings
Authors: Kukačková Helena | Kalendová Andréa
Year: 2012
Type of publication: článek v odborném periodiku
Name of source: Journal of Physics and Chemistry of Solids
Publisher name: Pergamon-Elsevier Science Ltd.
Place: Oxford
Page from-to: 1556-1561
Titles:
Language Name Abstract Keywords
cze Nalezení mechanické odolnosti a korozně-inhibičních vlastností povrchově modifikovaných plniv polyanilinem v organických povlacích Práce je zaměřena na studium povrchové úpravy částic plniva polyanilinem a jejím vlivem na korozně-inhibiční vlastnosti v organických povlacích. Byly výbrány plniva s neizometrickým tvarem částic a jejich účinnost byla srovnávána s fosforčnanem hlinito-zinečnatým a PANI. Povrch částic plniva byl pokryt PANI vrstvou během oxidační polymerace anilinu. Modelové povlaky na bázi dvoukomponentní vodouředitelné epoxidové pryskyřice byly připraveny s obsahem 10 % OKP. Mechanické testy byly provedeny z důvodu zjištění odolnosti povlaků v případě mechanického poškození. Antikorozní účinnost byly zjištěna pomocí zrychlených korozních testů. polymery; elektronová mikroskopie; defekty; mechanické vlastnosti; povrchové vlastnosti
eng Investigation of mechanical resistance and corrosion-inhibition properties of surface-modified fillers with polyaniline in organic coatings This work is focused on study of surface treatment of filler particles with polyaniline (PANI) and the influence on corrosion-inhibition properties in organic coatings. For this reason fillers with non-isometric shape were selected and their efficiency was compared with zinc-aluminum orthophosphate and PANI. The surface of filler particles was covered with PANI-layer during chemical oxidative polymerization of aniline. Model coatings based on two-component waterborne epoxy resin with PVC of 10% were prepared. Mechanical tests were used for the evaluation of resistance of pigmented coatings against mechanical damage. Anticorrosive efficiency was evaluated on the basis of accelerated corrosion tests and immersion test. The corrosion tests were carried out in salt spray chamber and in condensation chamber containing sulfur dioxide. polymers; electron microscopy; defects; mechanical properties; surface properties

Departments

Other Parts

Map

en.mapy.cz

Services

Popular Links

© 2023 University of Pardubice, Studentská 95, 532 10 Pardubice 2
Phone: +420 466 036 111, 466 036 112, 466 036 113
Webmaster, RSS
Data box ID: f5vj9hu
Accessibility Statement
CC BY-NC-ND 4.0Creative CommonsAttributionNonCommercialNoDerivatives