Synthesis of Tungstate Pigments of the Formula MNd2W2O10 (M = Ni, Zn, Mn)
Authors: Blovská Veronika | Bělina Petr | Šulcová Petra
Year: 2013
Type of publication: článek v odborném periodiku
Name of source: Journal of Thermal Analysis and Calorimetry
Publisher name: Springer
Page from-to: 83-89
Titles:
Language Name Abstract Keywords
cze Syntéza wolframových pigmentů o složení MNd2W2O10 (M=Ni,Zn, Mn) Nové sloučeniny na bázi wolframanu byly syntetizovány ve smyslu jako šetrné pigmenty k životnímu prostředí. Pigmenty byly připraveny reakcí v pevné fázi. Tato práce je zaměřena na směsné wolframany kovu s d-nezapněnými orbitaly a neodymu (III). Optimální podmínky pro syntézu meziproduktů MWO4 (M = Ni , Zn , Mn), Nd2WO6 a konečné produkty byly stanoveny MNd2W2O10 pomocí TG / DTA analýzy směsí výchozích materiálů. Tepelná stabilita MNd2W2O10 (M = Ni , Zn , Mn) byla studována pomocí tepelné mikroskopie s automatickou analýzu obrazu. Tato hodnota je v rozmezí od 1085 stupňů C pro ZnNd2W2O10 až 1158 stupňů C ppro MnNd2W2O10. Následný výzkum byl zaměřen na vliv různých kovů wolframanů na barevné vlastnosti pigmentů MNd2W2O10. Všechny vzorky byly nalezeny v zajímavých barevných odstínech, které byly získány pro Mn okr-žlutá, pro Ni hnědá a Zn světle fialová. Vliv mletí konečných pigmentů v planetovém mlýnu na barevné vlastnosti a distribuce velikosti částic byly hodnoceny . Anorganický pigment;reakce v pevné fázi;TG/DTA;kovové wolframany s nezapněnými d-orbitaly;wolframan neodymu (III)
eng Synthesis of Tungstate Pigments of the Formula MNd2W2O10 (M = Ni, Zn, Mn) New compounds based on tungstate were synthesized as environmentally friendly inorganic pigments. The pigments have been prepared by the solid state reaction. This work is focused on mixed d-block metal and neodymium(III) tungstate. The optimum conditions for synthesis of intermediate products MWO4 (M = Ni, Zn, Mn), Nd2WO6 and final products MNd2W2O10 were determined by TG/DTA analysis of starting materials mixtures. The thermal stability of MNd2W2O10 (M = Ni, Zn, Mn) was studied by heat microscopy with automatic image analysis. This value is at interval from 1,085 degrees C for ZnNd2W2O10 to 1,158 degrees C for MnNd2W2O10. Subsequent research was focused on the influence of d-block metals tungstates on the colour properties of the MNd2W2O10 pigments. All samples were found in interesting colour hues that were obtained for Mn ochre-yellow, for Ni brown and for Zn light violet. The effect of milling of final pigments in planetary mill on colour properties and particle size distribution was evaluated. Inorganic Pigment;Solid State Reaction;TG/DTA;d-Block Metal Tungstates;Neodymium (III) Tungstate

Departments

Other Parts

Map

en.mapy.cz

Services

Popular Links

© 2023 University of Pardubice, Studentská 95, 532 10 Pardubice 2
Phone: +420 466 036 111, 466 036 112, 466 036 113
Webmaster, RSS
Data box ID: f5vj9hu
Accessibility Statement
CC BY-NC-ND 4.0Creative CommonsAttributionNonCommercialNoDerivatives