Effect of the Synthesis Conditions on the Formation of MgSrP2O7 and its Characterisation for Pigmentary Application
Year: 2013
Type of publication: článek v odborném periodiku
Name of source: Journal of Thermal Analysis and Calorimetry
Publisher name: Springer
Page from-to: 147-155
Titles:
Language Name Abstract Keywords
cze Vliv syntézních podmínek na formování MgSrP2O7 a jeho charakterizace pro pigmentářské použití V uvedeném výzkumu jsme zkoumali MgSrP2O7 jako nový pigment s důrazem na jeho použití jako inhibitor koroze. Byl zkoumán vliv podmínek syntézy na vlastnosti výrobku. Vzorky byly získány pomocí reakce v pevné fázi a různými homogenizačními metodami počátečních složek (ruční homogenizace, mokré (ethanol/aceton) mletí s koulemi a spolusrážení). Tepelné chování reakčních směsí a sušeného coprecipitátoru bylo zkoumáno pomocí diferenční termické a termo-gravimetrické analýzy. Získané vzorky byly charakterizovány pomocí rentgenové difrakční analýzy, skenovací elektronové mikroskopie a IR spektroskopie. Zaměření na pigmentové použití, specifické vlastnosti vzorků byly vyhodnoceny, formou jako je tepelná stabilita, střední hodnoty velikosti částic a barevné parametry, a také byly provedeny předběžné antikorozní testy. Ze získaných výsledků by MgSrP2O7 mohl být považován za perspektivní inhibitor koroze a homogenizace přes koprecipitací může být vyhodnocen jako nejlepší způsob přípravy této kompozice, která poskytuje nejlepší tepelnou stabilitu, což je nejnižší velikosti částic, nejlepší homogenitu a nejslibnější vlastnosti proti korozi (pH a hustota vodné suspenze pigmentu) na konečný produkt . Pyrofosfát;environmentálně příznivý korozní inhibiční pigment;reakce v pevné fázi;korozní test
eng Effect of the Synthesis Conditions on the Formation of MgSrP2O7 and its Characterisation for Pigmentary Application In present research, we examined MgSrP2O7 as a new pigment with focus on its application as a corrosion inhibitor. The influence of the synthesis conditions on the product properties was examined. Samples were obtained by solid-state reaction and various homogenisation methods of initial components were employed (hand-milling, wet (ethanol/acetone) ball-milling and coprecipitation). Thermal behaviour of the reaction mixtures or dried coprecipitate was investigated using differential thermal and thermo-gravimetric analyses. Obtained samples were characterised with X-ray diffraction analysis, scanning electron microscopy and IR spectroscopy. Focusing on pigmentary application, specific properties of the samples were evaluated, such as thermal stability, mean particle size values and colour parameters, and also preliminary anticorrosion tests have been performed. Based on obtained results, MgSrP2O7 could be considered as a perspective corrosion inhibitor and homogenisation via coprecipitation can be rated as the best method of preparation of this composition, which provides the best thermal stability, the lowest particle size, the best homogeneity and the most promising corrosion inhibition characteristics (pH and rho of the pigment aqua suspension) for the final product. Pyrophosphate;Environmentally Friendly Corrosion Inhibition Pigment;Solid-State Reaction;Corrosion Test

Departments

Other Parts

Map

en.mapy.cz

Services

Popular Links

© 2023 University of Pardubice, Studentská 95, 532 10 Pardubice 2
Phone: +420 466 036 111, 466 036 112, 466 036 113
Webmaster, RSS
Data box ID: f5vj9hu
Accessibility Statement
CC BY-NC-ND 4.0Creative CommonsAttributionNonCommercialNoDerivatives