New Inorganic Pigments Based on SrSnO3 Doped by V2O5
Authors: Adolfová Lucie | Dohnalová Žaneta | Šulcová Petra
Year: 2013
Type of publication: článek v odborném periodiku
Name of source: Journal of Thermal Analysis and Calorimetry
Publisher name: Springer
Page from-to: 161-167
Titles:
Language Name Abstract Keywords
cze Nové anorganické pigmenty na bázi SrSnO3 dopované V2O5 Záměrem této práce bylo připravit sérii pigmentů SrVxSn1-xO3 (x=0; 0.025; 0.05; 0.1; 0.2 a 0.3) pomocí klasické keramické metody a suspenzním mísením surovin v teplotním intervalu 1 300- 1 500 °C. Tyto sloučeniny patří do skupiny vysokoteplotních pigmentů. Podstatou těchto pigmentů je tvorba hostitelské mřížky, která je dopována ionty vanadu. Toto začlenění iontů vede k získání pigmentů se zajímavou žlutou barvou po aplikaci do organického pojiva. Připravené pigmenty byly charakterizovány pomocí TG-DTA analýzy, skanovaní elektronové mikroskopiea měřením barevnosti. Velikost částic byla stanovena také. Fázová analýza byla provedena také s cílem definovat charakter nových sloučenin. Pigmenty světle žluté barvy byly získány pro koncentrace V 0.025 a kalcinační teploty 1475 °C. Termická analýza;perovskitová struktura;barva;pigment;keramický pigment;velikost částic
eng New Inorganic Pigments Based on SrSnO3 Doped by V2O5 The purpose of the present work was to prepare a series of pigments SrVxSn1-xO3 (x = 0; 0.025; 0.05; 0.1; 0.2 and 0.3) by classical ceramic method and by simulation of 'mixer dryer reactor' in the temperature range 1,300-1,500 degrees C. These compounds belong to group of high-temperature pigments. The principal of these pigments makes the host lattice of the SrSnO3, which is doped by vanadium ions. This incorporation of the doped ions leads to obtaining of the interesting yellow colour after application into the organic matrix. The fired pigments were characterised by TG-DTA analysis, scanning electron microscopy and colour measurements. The particle size was measured and X-ray diffraction analysis was also performed to define character of the new compounds. Pigments of brighter yellow colour were obtained for the V concentration 0.025 at calcination temperature 1,475 degrees C. Thermal Analysis;Perovskite Structure;Colour;Pigment;Ceramic Pigment;Particle Size

Departments

Other Parts

Map

en.mapy.cz

Services

Popular Links

© 2023 University of Pardubice, Studentská 95, 532 10 Pardubice 2
Phone: +420 466 036 111, 466 036 112, 466 036 113
Webmaster, RSS
Data box ID: f5vj9hu
Accessibility Statement
CC BY-NC-ND 4.0Creative CommonsAttributionNonCommercialNoDerivatives