High-temperature Reactions in the Co3Cr4(PO4)6-Cr(PO3)3 System: New Compound CoCr2(P2O7)2 and its Properties
Authors: Bosacka Monika | Blonska-Tabero Anna | Filipek Elzbieta | Luxová Jana | Šulcová Petra
Year: 2017
Type of publication: článek v odborném periodiku
Name of source: Journal of Thermal Analysis and Calorimetry
Publisher name: Springer
Place: Heidelberg
Page from-to: 95-101
Titles:
Language Name Abstract Keywords
cze Vysokoteplotní reakce v systému Co3Cr4(PO4)6 -Cr(PO3)3: Nová sloučenina CoCr2(P2O7)2 a její vlastnosti V systému Co3Cr4(PO4)6 -Cr(PO3)3 byl detekován nový difosfát (V) dichromito (III)- kobaltnatý (II) se vzorcem CoCr2(P2O7)2. Nová sloučenina byla získána v důsledku vysokoteplotních reakcí v tuhém stavu mezi CoCO3, Cr2O3 a (NH4)2HPO4 stejně jako mezi Cr(PO3)3 a Co3Cr4(PO4)6. CoCr2(P2O7)2 byl charakterizován metodami XRD, DTA a IR. Výsledky ukázaly, že CoCr2(P2O7)(2) krystaluje v triclinickém systému a byly vypočítány jeho buňkové parametry. Bylo prezentováno jeho infračervené spektrum. CoCr2(P2O7)2 taje inkongruentně při 1270+/-10 °C s tvorbou tuhého alfa-CrPO4. Sloučenina Co3Cr4(PO4)6, součást studovaného systému, byla poprvé získána jako čistá fáze. Jeho tepelná stabilita byla také zkoumána. Co3Cr4(PO4)6 je na vzduchu stabilní až do 1410 +/- 20 °C. Fosfát kobaltnato chromitý; Systém CoO-P2O5-Cr2O3; CoCr2(P2O7)2; XRD; DTA; IR
eng High-temperature Reactions in the Co3Cr4(PO4)6-Cr(PO3)3 System: New Compound CoCr2(P2O7)2 and its Properties A new dichromium(III) cobalt(II) diphosphate(V) of the formula CoCr2(P2O7)2 was detected in the Co3Cr4(PO4)6-Cr(PO3)3 system. The new compound was obtained as a result of high-temperature solid-state reactions between CoCO3, Cr2O3 and (NH4)2HPO4 as well as between Cr(PO3)3 and Co3Cr4(PO4)6. CoCr2(P2O7)2 was characterized using XRD, DTA and IR methods. Results demonstrated that CoCr2(P2O7)2 crystallizes in the triclinic system and its unit cell parameters were calculated. Its infrared spectrum was presented. CoCr2(P2O7)2 melts incongruently at 1270 +/- 10 degrees C with a formation of solid alpha-CrPO4. The compound Co3Cr4(PO4)6, component of the system under study, was obtained for the first time as a pure phase. Its thermal stability was also investigated. Co3Cr4(PO4)6 is stable in air up to 1410 +/- 20 degrees C. Chromium cobalt phosphate; System CoO-P2O5-Cr2O3; CoCr2(P2O7)2; XRD; DTA; IR

Departments

Other Parts

Map

en.mapy.cz

Services

Popular Links

© 2023 University of Pardubice, Studentská 95, 532 10 Pardubice 2
Phone: +420 466 036 111, 466 036 112, 466 036 113
Webmaster, RSS
Data box ID: f5vj9hu
Accessibility Statement
CC BY-NC-ND 4.0Creative CommonsAttributionNonCommercialNoDerivatives