Comparison of photoelectrochemical performance of anodic single- and double-walled TiO2 nanotube layers
Authors: Motola Martin | Sopha Hanna Ingrid | Krbal Miloš | Hromádko Luděk | Olmrová Zmrhalová Zuzana | Plesch Gustav | Macák Jan
Year: 2018
Type of publication: článek v odborném periodiku
Name of source: Electrochemistry Communications
Page from-to: 1-5
Titles:
Language Name Abstract Keywords
cze Porovnání fotoelektrochemických vlastností anodických jedno- a dvou-stěnných nanotrubiček TiO2 V této práci byly porovnávány fotoelektrochemické vlastnosti s jednou (SW) a dvěmi (DW) stěnami TiO2 nanotrubic (TNT). Za pomoci anodizace byly narostlé TNT vrstvy na Ti substrátu ve dvou různých elektrolytech na bázi etylén glykolu. Bylo dosaženo tloušťky TNT vrstev ≈5 a ≈15 µm . Vnitřní stěna TNT byla kvantitativně odstraněna za pomoci předžíhání a následným chemickým leptáním v roztoku piraňa. Na všech TNT vrstvách byly zkoumané jejich foto-elektrochemické vlastnosti v ultrafialovém a blízko viditelném spektru záření. Výrazné zlepšení hustoty fotoproudu bylo pozorováno pro SW-TNT vrstvy. Toto je možno připsat zvýšené separaci nositelů náboje ve stěnách nanotrubek z důvodu odstranění vnitřní stěny, bohaté na C a F, za pomoci leptání. Oxid titaničitý; Nanotrubice; Jednostěnné; Dvoustěnné; Fotoelektrochemie
eng Comparison of photoelectrochemical performance of anodic single- and double-walled TiO2 nanotube layers In this work, the photoelectrochemical response of single-walled (SW) and double-walled (DW) TiO2 nanotube (TNT) layers is presented. TNT layers were grown on Ti substrates by anodization in two different ethylene glycol-based electrolytes to obtain ~5 and ~15 μm thick TNT layers. The inner shell of the TNT was quantitatively removed via a mild pre-annealing followed by a selective chemical etching treatment in piranha solution. All TNT layers were investigated for their photoelectrochemical response in the ultraviolet and near visible spectral range. Significantly enhanced photocurrent densities were revealed for the SW-TNT layers. This is ascribed to improved charge carrier separation along the tube walls due to the lack of the C- and F-rich inner shell removed by etching. Titanium dioxide; Nanotubes; Single-walled; Double-walled; Photoelectrochemistry

Departments

Other Parts

Map

en.mapy.cz

Services

Popular Links

© 2023 University of Pardubice, Studentská 95, 532 10 Pardubice 2
Phone: +420 466 036 111, 466 036 112, 466 036 113
Webmaster, RSS
Data box ID: f5vj9hu
Accessibility Statement
CC BY-NC-ND 4.0Creative CommonsAttributionNonCommercialNoDerivatives