Nd3+: Ga-Ge-Sb-S glasses and fibers for luminescence in mid-IR: synthesis, structural characterization and rare earth spectroscopy

Year: 2018

Type of publication: článek v odborném periodiku

Name of source: Optical Materials Express

Publisher name: Optical Society of America

Place: Washington, DC

Page from-to: 1650-1671

Titles:

Language	Name	Abstract	Keywords
cze	Skla a vlákna Nd3+: Ga-Ge-Sb-S pro luminiscenci v MID-IR: syntéza, strukturní charakterizace a spektroskopie vzácné zeminy	Pro objemová skla Ga-Ge-Sb-S byla měřena teplota skelného přechodu, hustota, koeficient teplotní roztažnosti a index lomu v blízké a střední infračervené oblasti spektra. Struktura skelné sítě byla analyzována spektrometrií Ramanova rozptylu, Ga-71 NMR a EXAFS, K-hrana Ga, Ge, Sb, S a Nd. Absorpční a emisní spektra neodymem dopovaných sulfidových skel byla zaznamenána od viditelné oblasti po MID-IR. Pro některé přechody byly změřeny doby života excitovaných stavů. Doby života klesají s koncentrací Nd3+, zvláště pro hladiny 4I13/2 a 4I11/2. Spektroskopické parametry byly stanoveny Judd-Ofeltovou metodou, která umožňuje výpočet emisních průřezů a určení kvantových výtěžků. Byla také provedena měření optického útlumu a emisní měření optických vláken s širokým emisním pásem 4.7-5.7 mikrometrů v MID-IR.	chalkogenidová skla; iont Nd3+; luminiscence; optická vlákna
eng	Nd3+: Ga-Ge-Sb-S glasses and fibers for luminescence in mid-IR: synthesis, structural characterization and rare earth spectroscopy	The glass transition temperature, density, expansion coefficient, and near and mid-IR refractive indexes were measured on bulk Ga-Ge-Sb-S glass samples. Their glass network structures were analyzed by Raman scattering spectrometry, NMR of Ga-71 and EXAFS, K-edge of Ga, Ge, Sb, S and Nd. The absorption and emission spectra of neodymium doped sulfide glasses were recorded from the visible to the mid-IR. Excited state lifetimes were measured for several transitions. The lifetimes decrease with the concentration of Nd3+, especially for the 4I13/2 and 4I11/2 levels. The spectroscopic parameters were determined by the Judd-Ofelt method, allowing the calculation of cross-section emissions and the evaluation of quantum yields. Optical attenuation and emission measurements of fiber were also performed with a broad 4.7-5.7 mu m emission band in the mid-IR.	chalcogenide glasses; Nd3+ ion; luminescence; optical fibers