Tb3+ doped Ga5Ge20Sb10Se65-xTex (x=0-37.5) chalcogenide glasses and fibers for MWIR and LWIR emissions
Authors: Abdellaoui N. | Starecki F. | Boussard-Pledel C. | Shpotyuk Y. | Doualan J-L. | Braud A. | Baudet Emeline | Němec Petr | Chevire F. | Dussauze M. | Bureau B. | Camy P. | Nazabal Virginie
Year: 2018
Type of publication: článek v odborném periodiku
Name of source: Optical Materials Express
Publisher name: Optical Society of America
Place: Washington, DC
Page from-to: 2887-2900
Titles:
Language Name Abstract Keywords
cze Ga5Ge20Sb10Se65-xTex (x=0-37.5) chalkogenidová skla a vlákna dopovaná Tb3+ pro emise v MWIR a LWIR Byla syntetizována chalkogenidová skla s nominálním složením Ga5Ge20Sb10Se(65-x) Te-x (x = 0, 10, 20, 25, 30, 32.5, 35, 37.5). Byly studovány luminiscenční vlastnosti objemových skel a vláken Ga5Ge20Sb10Se65 a Ga5Ge20Sb10Se45Te20 dopovaných Tb3+ (500 ppm). Parametry zářivých přechodů vypočtené Judd-Ofeltovou teorií jsou porovnány s experimentálními daty. MID-IR emise v oblasti 4.3-6.0 mikrometrů je přiřazena přechodu 7F5->7F6 iontů Tb3+ s odpovídající experimentální dobou života 8.9 a 7.8 ms pro selenidovou a seleno-telluridovou skelnou matrici. Emise 7F4->7F6 byla zaznamenána při vlnové délce 3.1 mikrometru sd dobrým poměrem signálu k šumu, prokazující silnou emisi z hladiny 7F4. Přestože bylo očekáváno, že fononová energie bude nižší pro telluridová skla, selenidová skla jsou vhodnější pro emise v MWIR a LWIR s dobře definovanými emisními pásy od 3.1 do 8 mikrometrů. chalkogenidová skla; optická vlákna; luminiscence; iont Tb3+
eng Tb3+ doped Ga5Ge20Sb10Se65-xTex (x=0-37.5) chalcogenide glasses and fibers for MWIR and LWIR emissions Chalcogenide glasses with a nominal composition of Ga5Ge20Sb10Se(65-x) Te-x (x = 0, 10, 20, 25, 30, 32.5, 35, 37.5) were synthesized. The luminescence properties of Tb3+(500 ppm) doped Ga5Ge20Sb10Se65 and Ga5Ge20Sb10Se45Te20 bulk glasses and fibers were studied. Radiative transitions parameters calculated from the Judd-Ofelt theory are compared to the experimental values. Mid-IR emission in the range of 4.3-6.0 mu m is attributed to the 7F5->7F6 transition of Tb3+ ions with a corresponding experimental lifetime of 8.9 and 7.8 ms for the selenide and seleno-telluride matrix, respectively. The 7F4->7F6 emission was recorded at 3.1 mu m with a good signal-to-noise ratio, evidencing a rather strong emission from the 7F4 manifold. Finally, although it was expected that the phonon energy will be lower for telluride glasses, selenide glasses are still more suitable for mid-wavelength infrared and long wavelength infrared emissions with well-defined emissions from 3.1 to 8 mu m. chalcogenide glasses; optical fibers; luminescence; Tb3+ ion

Departments

Other Parts

Map

en.mapy.cz

Services

Popular Links

© 2023 University of Pardubice, Studentská 95, 532 10 Pardubice 2
Phone: +420 466 036 111, 466 036 112, 466 036 113
Webmaster, RSS
Data box ID: f5vj9hu
Accessibility Statement
CC BY-NC-ND 4.0Creative CommonsAttributionNonCommercialNoDerivatives