FeOx/Al2O3 Catalysts for High-temperature Decomposition of N2O Under Conditions of NH3 Oxidation in Nitric Acid Production
Authors: Sádovská Galina | Tabor Edyta | Bernauer Milan | Sazama Petr | Fila Vlastimil | Kmjec Tomas | Kohout Jaroslav | Zaveta Karel | Tokarova Věnceslava | Sobalik Zdeněk
Year: 2018
Type of publication: článek v odborném periodiku
Name of source: Catalysis Science and Technology
Publisher name: Royal Society of Chemistry
Place: Cambridge
Page from-to: 2841-2852
Titles:
Language Name Abstract Keywords
cze FeOx/Al2O3 katalyzátory pro vysokoteplotní rozklad N2O za podmínek oxidace NH3 ve výrobnách kyseliny dusičné Katalytická aktivita série katalyzátorů FeOx/Al2O3 připravených za různých podmínek byla testována pro vysokoteplotní rozklad N2O (HT-deN2O) v komplexní směsi vznijkající při spalování amoniaku, čímž byly simulovány podmínky z výroben kyseliny dusičné. Byla studována stabilita katalyzátorů během dlouhodobé (12 dní) zátěže. Jak čerstvě připravené, tak i zestárlé katalyzátory vykazovaly více než 90% konverzi N2O v teplotním rozsahu 750-900 °C. Strukturní analýza ukázala, že FeOx/Al2O3 katalyzátory obsahovaly různá množství δ, θ a α aluminy a až 4 druhy iontu železa. Ve formách δ a θ Al2O3 je dobře stabilůizováno Fe(III) v Td nebo Oh koordinaci, které bylo identifikováno jako aktivní centrum v HT-deN2O. FeOx/Al2O3;Katalýza;Vysokoteplotní rozklad;N2O;Alumina;Stabilita;Změny modifikací
eng FeOx/Al2O3 Catalysts for High-temperature Decomposition of N2O Under Conditions of NH3 Oxidation in Nitric Acid Production The catalytic activity of a series of FeOx/Al2O3 prepared under various conditions was evaluated for high temperature decomposition of N2O (HT-deN(2)O) in a complex gas mixture produced by oxidation of ammonia. Thus the relevant step in the industrial nitric acid production process was simulated. The catalyst stability during long-term exposure (12 days) to reaction conditions relevant to HT-deN(2)O was studied. Both fresh and aged FeOx/Al2O3 exhibited more than 90% conversion of N2O in the 750-900 degrees C temperature range. Structural analysis showed that the prepared FeOx/Al2O3 catalysts contained various proportions of , and alumina phases and up to four individual iron species. In the and Al2O3 phases, well stabilized Fe(iii) in T-d or O-h coordination was identified as the active species in HT-deN(2)O. FeOx/Al2O3;Catalysis;High-temperature decomposition;N2O;Alumina;Stability;Modification changes

Departments

Other Parts

Map

en.mapy.cz

Services

Popular Links

© 2023 University of Pardubice, Studentská 95, 532 10 Pardubice 2
Phone: +420 466 036 111, 466 036 112, 466 036 113
Webmaster, RSS
Data box ID: f5vj9hu
Accessibility Statement
CC BY-NC-ND 4.0Creative CommonsAttributionNonCommercialNoDerivatives