Crystallization of (GeSe2)(0.3)(Sb2Se3)(0.7) chalcogenide glass - Influence of reaction atmosphere
Authors: Svoboda Roman
Year: 2019
Type of publication: článek v odborném periodiku
Name of source: Journal of Non-Crystalline Solids
Publisher name: Elsevier Science BV
Place: Amsterdam
Page from-to: 23-30
Titles:
Language Name Abstract Keywords
cze Krystalizace (GeSe2)(0.3)(Sb2Se3)(0.7) chalkogenidového skla - vliv reakční atmosféry Studium vlivu reakční atmosféry na krystalizační chování (GeSe2)(0.3)(Sb2Se3)(0.7) skla bylo provedeno pomocí DSC, IR mikroskopie a XRD. Bylo zjištěno, že přítomnost kyslíku v atmosféře vede k akceleraci růstu krystalů na povrchu i v objemu materiálu. podobný efekt byl pozorován u prášků i objemových skel. krystalizace; reakční atmosféra; DSc; XRD; mikroskopie; (GeSe2)(0.3)(Sb2Se3)(0.7) sklo
eng Crystallization of (GeSe2)(0.3)(Sb2Se3)(0.7) chalcogenide glass - Influence of reaction atmosphere Differential scanning calorimetry, infrared microscopy and X-ray diffraction analysis and were used to investigate the influence of reaction atmosphere (air versus pure nitrogen) on crystallization behavior of (GeSe2)(0.3)(Sb2Se3)(0.7) glass. The presence of oxygen was found to accelerate the crystal growth both on surface and in bulk material, with a similar effect in case of powders and bulk samples. Detailed crystallization kinetics study was performed, revealing that the presence of oxygen leads to a lowered activation energy and steeper onset of the process single-curve-averaged masterplot approach was used to deal with the temperature-differentiated complexity of the crystallization. Direct observations by infrared microscopy have shown that the presence of oxygen leads to a formation of robust surface crystalline layer, which prevents powder sintering and bulk samples deformation by viscous flow, and to a more rapid nucleation and crystal growth within the sample volume. Based on the viscosity values estimated for the crystallization temperatures, an explanation for the accelerated volume crystallization was proposed, employing the quasi-stationary conditions contributing to better cohesivity of critical nuclei and crystal/glass interface. The existence of the surface crystalline layer however prevents the sample from reaching full crystallinity. Crystallization kinetics; Reaction atmosphere; DSC; XRD; Infrared microscopy; (GeS2)(0.3)(Sh(2)S(3))(0.7) glass

Departments

Other Parts

Map

en.mapy.cz

Services

Popular Links

© 2023 University of Pardubice, Studentská 95, 532 10 Pardubice 2
Phone: +420 466 036 111, 466 036 112, 466 036 113
Webmaster, RSS
Data box ID: f5vj9hu
Accessibility Statement
CC BY-NC-ND 4.0Creative CommonsAttributionNonCommercialNoDerivatives