Thermoanalytical study and crystallization of Ba(PO3)(2)-WO3 glasses
Year: 2019
Type of publication: článek v odborném periodiku
Name of source: Journal of Thermal Analysis and Calorimetry
Publisher name: Springer
Place: Heidelberg
Page from-to: 1911-1918
Titles:
Language Name Abstract Keywords
cze Termoanalytická studie a krystalizace skel Ba(PO3)(2)-WO3 Byla připravena a studována fosfátová skla barnatá systému (100 - x)Ba(PO3)(2)-xWO(3) s obsahem 0-60 mol.% WO3. Termické vlastnosti těchto skel byly studovány pomocí DTA, dilatometrie a žárové mikroskopie. Teplota skelné transformace ve sklech této kompoziční řady roste s rostoucím obsahem WO3 v rozmezí 461 °C (x = 0) až 623 °C (x = 60). Většina skel během zahřívání krystalizuje v rozmezí 650-750 °Cs vyjímkou skel obsahujících 20-30 mol.% WO3, která jsou termicky stabilní. Byla zjištěna vysoká chemická odolnost těchto skel. Studiem krystalizace těchto skel byla rovněž zjištěna nová sloučenina Ba(WO2)2(PO4)2. Tato sloučenina patří do hexagonální soustavy s parametry elementární buňky a = 13.8600(2) Å, b = 12.3207(2) Å, c = 6.3529(1)Å, β = 120.86(1)°, V = 931.3(4) Å3 a bodem tání 936 °C. Ramanova spektroskopie poukázala na částečný amorfní charakter některých zakrystalovaných vzorků. 31P MAS BNR ukázala na přítomnost pouze jediné koordinace atomů fosforu ve sloučenině Ba(WO2)2(PO4)2. fosfátová skla; termické vlastnosti; fyzikální vlastnosti; krystalizace
eng Thermoanalytical study and crystallization of Ba(PO3)(2)-WO3 glasses Barium phosphate glasses of the composition (100 - x)Ba(PO3)(2)-xWO(3) with 0-60 mol% WO3 were prepared and studied. Thermal studies of the glasses were carried out with DTA, dilatometry and hot-stage microscopy. Glass transition temperature in this glass series increases with increasing WO3 content from 461 degrees C (x = 0) to 623 degrees C (x = 60). Most glasses containing WO3 crystallize on heating within the range of 650-750 degrees C with the exception of glasses with 20-30 mol% WO3, which are thermally stable. Very high chemical durability of these glasses with dissolution rate of 1.4 x 10(-8)-6.2 x 10(-9) g cm(-2) min(-1) was also revealed. Crystallization of glasses revealed the existence of a new compound Ba(WO2)(2)(PO4)(2) in the studied compositional series. The compound Ba(WO2)(2)(PO4)(2) possess hexagonal unit cell of dimensions a = 11.5191(1) A and c = 6.3437(1) A, and its melting point is 936 degrees C. Raman spectra of crystallized glasses confirmed the formation of crystalline compound in this glass series and revealed the presence of glass phase in some thermal-treated samples. P-31 MAS NMR showed on only one coordination of phosphorus atoms in the Ba(WO2)(2)(PO4)(2) compound. Phosphate glasses; Thermal properties; Physical properties; Crystallization

Departments

Other Parts

Map

en.mapy.cz

Services

Popular Links

© 2023 University of Pardubice, Studentská 95, 532 10 Pardubice 2
Phone: +420 466 036 111, 466 036 112, 466 036 113
Webmaster, RSS
Data box ID: f5vj9hu
Accessibility Statement
CC BY-NC-ND 4.0Creative CommonsAttributionNonCommercialNoDerivatives