Ti3+ doped anodic single-wall TiO2 nanotubes as highly efficient photocatalyst
Authors: Motola Martin | Caplovicova Maria | Krbal Miloš | Sopha Hanna Ingrid | Thirunavukkarasu Guru Karthikeyan | Gregor Maros | Plesch Gustav | Macák Jan
Year: 2020
Type of publication: článek v odborném periodiku
Name of source: Electrochimica Acta
Publisher name: Elsevier Science
Place: Oxford
Page from-to: "135374-1"-"135374-8"
Titles:
Language Name Abstract Keywords
cze Anodické TiO2 nanotrubice s jednou stěnou, dopované Ti3+, jako vysoce účinný katalyzátor Tato práce prezentuje nový dvoustupňový postup modifikace vrstev TiO2 nanotrubic (TNT) směrem k vylepšené fotokatalytické odezvě. TNT vrstvy o tloušťce 7 mikrometrů a vnitřním průměru 190 nm byly připraveny elektrochemickou anodizací Ti fólií v roztocích ethylenglykolu s přídavkem fluoridů. Následně byly podrobeny dvoustupňové modifikaci. Nejprve byly odstraněna vnitřní stěna trubic pomocí jemného přežahu a selektivního leptání v roztoku piraňa. Poté byly trubice žíhány v redukující atmosféře vodíku a argonu. Výsledné vrstvy TNT, dopované Ti3+, vykazovaly 100%ní navýšení fototokatalytické aktivity oproti neupraveným vrstvám. TiO2 nanotrubice; trubice s jednou stěnou; povrchová redukce; fotoelektrochemie; fotokatalýza
eng Ti3+ doped anodic single-wall TiO2 nanotubes as highly efficient photocatalyst In this work, a two-step treatment of TiO2 nanotube (TNT) layers towards enhanced photocatalytic performance is presented. TNT layers with a thickness of similar to 7 mu m and an average inner diameter of similar to 190 nm were prepared via electrochemical anodization of Ti foil in a fluoride containing ethylene glycolbased electrolyte. To improve the photocatalytic activity of the produced TNT layers a two-step post-treatment was conducted. First, the inner shell of the native double-wall TNT layers was removed via a mild pre-annealing followed by a selective etching treatment of the inner shell in piranha solution yielding single-wall TNT layers. Second, reduction via annealing in H-2/Ar atmosphere was performed. The resulting Ti3+ doped single-wall TNT layers possess 100% enhancement of photocatalytic activity compared to their non-treated counterparts. (C) 2019 Elsevier Ltd. All rights reserved. TiO2 nanotube layers; Single-wall; H-2 Surface reduction; Photoelectrochemistry; Photocatalysis

Departments

Other Parts

Map

en.mapy.cz

Services

Popular Links

© 2023 University of Pardubice, Studentská 95, 532 10 Pardubice 2
Phone: +420 466 036 111, 466 036 112, 466 036 113
Webmaster, RSS
Data box ID: f5vj9hu
Accessibility Statement
CC BY-NC-ND 4.0