Mechanical and anticorrosion efficiency of organic coatings with polyaniline phosphate and polypyrrole phosphate modified pigments
Year: 2020
Type of publication: článek v odborném periodiku
Name of source: Ochrona Przed Korozja
Publisher name: Wydawnictvo SIGMA-NOT
Place: Varšava
Page from-to: 278-289
Titles:
Language Name Abstract Keywords
cze Mechanická a antikorozní účinnost organických povlaků s pigmenty modifikovanými polyanilin fosfátem a polypyrol fosfátem Tento článek popisuje výsledky studie antikorozní účinnosti kompozitních materiálů potažených solemi vodivých polymerů solí na povrchu syntetizovaných pigmentových částic. Konkrétně byly připraveny kompozitní pigmenty s polyanilin fosfátem a polypyrol fosfátem. Novinka spočívá v testování antikorozních vlastností kompozitních pigmentů na bázi wolframu a molybdenanu, které byly povrchově upraveny solemi vodivých polymerů. Byly syntetizovány a popsány molybdenany a wolframany které byly potaženy solemi vodivých polymerů. Bylo připraveno a popsáno dvanáct vzorků kompozitních pigmentů a byly formulovány barvy, které je obsahují jako pigmenty. Jako pojivo sloužila epoxyesterová pryskyřice rozpouštědlového typu. Objemové koncentrace kompozitních pigmentů v barvě byly 1%, 5%, 10% a 15%. Barvy byly naneseny na ocelové panely a byla měřena antikorozní účinnost kompozitních pigmentů v závislosti na typu soli vodivého polymeru a objemové koncentraci pigmentu. Jako referenční materiály byly připraveny vzorky barev obsahující komerční pigment fosforečnan zinečnatý. Byly také měřeny fyzikálně-mechanické vlastnosti barev: lakové filmy vykazovaly vynikající mechanickou odolnost. Nátěrové filmy byly podrobeny zrychleným cyklickým korozním testům, výsledky ukazují na velmi dobrou antikorozní účinnost organických povlaků obsahujících zkoušené kompozitní pigmenty. organický povlak; polyanilin fosfát; polypyrol fosfát; epoxyesterová pryskyřice; molybdenan; wolframan
eng Mechanical and anticorrosion efficiency of organic coatings with polyaniline phosphate and polypyrrole phosphate modified pigments This paper describes the results of a study of the anticorrosion efficiency of composite materials prepared by precipitating conductive polymer salts on the surface of synthesized pigment particles. Specifically, composite pigments with polyaniline phosphate and polypyrrole phosphate were prepared. The novelty consists in testing the anticorrosive properties of composite pigments based on tungsten and molybdate, which have been surface treated with salt conductive polymers. Strontium, zinc and ferric molybdates and tungstates were synthesized and described and then coated with the conductive polymer salts. Twelve composite material samples were prepared and described and paints containing them as pigments were formulated. A solvent-type epoxy-ester resin served as the binder. The volume concentrations of the composite materials in the paint were 1%, 5%, 10% and 15%. The paints were applied to steel panels and the anticorrosion efficiency of the composite pigments was measured in dependence on the conductive polymer salt type and pigment volume concentration. Paint samples containing a commercial zinc phosphate pigment were prepared as reference materials. The physico-mechanical properties of the paints were also measured: the paint films exhibited an outstanding mechanical resistance. The steel panels coated with the paints were subjected to accelerated cyclic corrosion tests, the results point to a very good anticorrosion efficiency of the organic coatings containing the composite particles examined. organic coating; polyanilin phosphate; polypyrrol phosphate; epoxyester resin; molybdate; tungstate

Departments

Other Parts

Map

en.mapy.cz

Services

Popular Links

© 2023 University of Pardubice, Studentská 95, 532 10 Pardubice 2
Phone: +420 466 036 111, 466 036 112, 466 036 113
Webmaster, RSS
Data box ID: f5vj9hu
Accessibility Statement
CC BY-NC-ND 4.0Creative CommonsAttributionNonCommercialNoDerivatives