Calorimetric Examination of Suitability of Calcium, Cobalt and Nickel Nitrate Hydrates for Thermal Energy Storage
Year: 2020
Type of publication: článek v odborném periodiku
Name of source: Journal of Thermal Analysis and Calorimetry
Publisher name: Springer
Place: Heidelberg
Page from-to: 275-287
Titles:
Language Name Abstract Keywords
cze Kalorimetrická studie vhodnosti hydrátu dusičnanu vápenatého, kobaltnatého a nikelnatého pro uchování tepelné energie Vybrané hydráty dusičnanů byly charakterizovány pomocí rentgenové difrakce, heliového pyknometru, kalorimetru Calvetova typu a simultánní termogravimetrie s diferenční skenovací kalorimetrií. Tání a krystalizace všech studovaných hydrátů dusičnanů bylysledovány pomocí DSC a podchlazení (rozdíl mezi teplotou tání a krystalizační teplotou) bylo stanoveno na více než 80, 14 a 37 °C pro dusičnan vápenatý tetrahydrát a dusičnan kobaltnatý a nikelnatý hexahydrát. Tyto soli byly míchány s vybranými nukleačními činidly k potlačení podchlazení a poté testovány opakovanými cykly ohřev- chlazení. Dusičnan vápenatý tetrahydrát poskytuje vratný proces (l)-(s) s přídavkem CaO, Ca(OH)2, BaO, Ba(OH)28H2O, grafitu a grafenu, ale i tak zůstává podchlazení příliš vysoké a zároveň klesá hodnota entalpie sledované fázové změny. V případě dusičnanu kobaltnatého hexahydrátu je nejvhodnějším nukleačním činidlem CaO, Ba(OH)28H2O a grafit a to v přídavku 1 hm%. Podchlazení u dusičnanu nikelnatého hexahydrátu bylo výrazně sníženo přídavkem CaO, Sr(OH)2 a grafitu. Hydrát dusičnanu kobaltnatého a nikelnatého byl testován také s přídavkem dvou nukleačních činidel dohromady (1:1). Nejlepších výsledků bylo dosaženo pro složení s 1 hm% nukleačního činidla tvořeného grafitem a Ba(OH)28H2O pro kobaltnatou sůl a CaO s Mg(OH)2 pro nikelnatou sůl. Dusičnan vápenatý tetrahydrát;Dusičnan kobaltnatý hexahydrát;Dusičnan nikelnatý hexahydrát;Dehydratace;Látky s fázovou změnou;DSC;Nukleační činidlo;Podchlazení
eng Calorimetric Examination of Suitability of Calcium, Cobalt and Nickel Nitrate Hydrates for Thermal Energy Storage Selected nitrate hydrates were characterized using X-ray diffraction, helium pycnometer, Calvet-type calorimeter and simultaneous thermogravimetry coupled with differential scanning calorimeter. Melting and crystallization of all studied nitrate hydrates were observed by differential scanning calorimeter, and the supercooling (difference between melting temperature and crystallization temperature) was found to be more than 80, 14 and 37 degrees C for calcium nitrate tetrahydrate, cobalt and nickel nitrate hexahydrates, respectively. Those salts were mixed with selected nucleating agents to suppress supercooling and then tested under repeating of heating-cooling cycles. Calcium nitrate tetrahydrate showed reversible liquid-solid process with addition of CaO, Ca(OH)(2), BaO, Ba(OH)(2)center dot 8H(2)O, graphite and graphene, but the supercooling remains too high, and the enthalpy change significantly decreased. In the case of cobalt nitrate hexahydrate, the CaO, Ba(OH)(2)center dot 8H(2)O and graphite are the most effective nucleating agent in amount of 1 mass%. The supercooling of nickel nitrate hexahydrate was effectively reduced by addition of CaO, Sr(OH)(2) and graphite. The cobalt and nickel nitrates were tested with combination of two nucleating agents (1:1). The best results were obtained for composites with addition of 1 mass% of nucleating agent mixture consisting of both graphite and Ba(OH)(2)center dot 8H(2)O for cobalt nitrate hexahydrate, and CaO with Mg(OH)(2) for nickel nitrate hexahydrate. Calcium nitrate tetrahydrate;Cobalt nitrate hexahydrate;Nickel nitrate hexahydrate;Dehydration;Phase-change materials;DSC;Nucleating agent;Supercooling

Departments

Other Parts

Map

en.mapy.cz

Services

Popular Links

© 2023 University of Pardubice, Studentská 95, 532 10 Pardubice 2
Phone: +420 466 036 111, 466 036 112, 466 036 113
Webmaster, RSS
Data box ID: f5vj9hu
Accessibility Statement
CC BY-NC-ND 4.0