Scaling up anodic TiO2 nanotube layers - Influence of the nanotube layer thickness on the photocatalytic degradation of hexane and benzene

Year: 2022

Type of publication: článek v odborném periodiku

Name of source: Applied Materials Today

Publisher name: Elsevier Science BV

Place: Amsterdam

Page from-to: 101567

Titles:

Language	Name	Abstract	Keywords
cze	Zvětšování ploch vrstev anodických nanotrubiček TiO2 - Vliv tloušťky vrstvy nanotrubiček na fotokatalytickou degradaci hexanu a benzenu	V této práci je poprvé ukázána příprava homogenních vrstev TiO2 nanotrubic (TNT) o různých tloušťkách, pomocí anodizace na Ti substrátech s velkou geometrickou plochou - dvakrát 5 cm x 10 cm (tj. obě strany Ti substrátu). Vrstvy TNT se čtyřmi různými tloušťkami (0,65 µm, 1 µm, 7 µm a 14 µm) byly připraveny s vynikající konformitou a homogenitou na eloxované ploše. Tyto vrstvy TNT byly úspěšně použity jako fotokatalyzátory pro degradaci hexanu a benzenu, jako modelových sloučenin v plynné fázi, podle norem ISO, což ukazuje na zvýšení konverze pro obě modelové sloučeniny s tloušťkou vrstvy TNT. Zatímco u všech vrstev TNT byla během doby měření tří hodin pozorována stabilní konverze hexanu, v případě degradace benzenu byl sledován počáteční pokles konverze, než se konverze stabilizovala. Navzdory tomuto trendu, analýzy SEM a XPS neodhalily žádné významné množství reakčních produktů na povrchu vrstvy TNT.	vrstvy nanotrubiček; TiO2,anodizace; velké plochy; upscaling; plynovéfáze fotokatalýza
eng	Scaling up anodic TiO2 nanotube layers - Influence of the nanotube layer thickness on the photocatalytic degradation of hexane and benzene	In this work, the preparation of homogenous TiO2 nanotube (TNT) layers with different thicknesses via anodization on Ti substrates with a large geometrical area of two times 5 cm x 10 cm (i.e. both sides of the Ti substrate) is shown for the first time. TNT layers with four different thicknesses of similar to 0.65 µm, similar to 1 µm, similar to 7 µm, and similar to 14 µm were prepared with excellent conformality and homogeneity over the anodized area. These TNT layers were successfully employed as photocatalysts for the degradation of hexane and benzene as model compounds in the gas phase under ISO standards, showing an increase of the conversion for both model compounds with the TNT layer thickness. While a stable hexane conversion was observed for all TNT layers during the measuring time of three hours, in case of benzene degradation an initial conversion decrease was monitored before the conversion stabilized. Despite this trend, SEM and XPS analyses did not reveal any significant amount of reaction products on the TNT layer surface.	TiO2 nanotube layers; anodization; large areas; upscaling; gasphase photocatalysis