Assessment of Destructive and Nondestructive Analysis for GGBS Based Geopolymer Concrete and Its Statistical Analysis
Authors: Shilar Fatheali A | Ganachari Sharanabasava, V | Patil Veerabhadragouda B. | Javed Syed | Khan T. M. Yunus | Baig Rahmath Ulla
Year: 2022
Type of publication: článek v odborném periodiku
Name of source: Polymers
Publisher name: MDPI
Place: BASEL
Page from-to: 3132
Titles:
Language Name Abstract Keywords
cze Posouzení destruktivní a nedestruktivní analýzy pro geopolymerní beton na bázi GGBS a jeho statistická analýza Geopolymer je alternativou k současným trendům ve stavebních materiálech. V tomto článku je učiněn pokus o výrobu udržitelného konstrukčního kompozitního materiálu pomocí geopolymeru. Geopolymerní beton na bázi mleté granulované vysokopecní strusky (GGBS) byl připraven a testován na různé poměry alkálie k pojivu (A/B). Byl hodnocen vliv různých teplot na pevnostní vlastnosti v tlaku. Kostky byly vystaveny teplotě v rozmezí 50 až 70 stupňů C po dobu 2 až 10 hodin a pevnost v tlaku vzorků byla analyzována pro destruktivní a nedestruktivní analýzu a testována po dobu 7, 28 a 90 dnů. Získané výsledky pevnosti v tlaku (CS) byly analyzovány pomocí křivky pravděpodobnosti (PP), křivky přehledu distribuce (DOC), funkce hustoty pravděpodobnosti (PDF), Weibullovy křivky, přežití a křivky rizikové funkce. Maximální pevnosti v tlaku bylo dosaženo pro teplotu 70 °C a A/B 0,45 pro destruktivní zkoušky a nedestruktivní zkoušky s 44,6 MPa a 43,56 MPa za 90 dnů zkoušení. Křivky přežití a funkce rizika ukázaly přírůstkové distribuční charakteristiky po 28 a 90 dnech výsledků testování s faktorem pravděpodobnosti v rozmezí od 0,8 do 1,0.
eng Assessment of Destructive and Nondestructive Analysis for GGBS Based Geopolymer Concrete and Its Statistical Analysis Geopolymer is the alternative to current construction material trends. In this paper, an attempt is made to produce a sustainable construction composite material using geopolymer. Ground granulated blast furnace slag (GGBS)-based geopolymer concrete was prepared and tested for different alkaline to binder ratios (A/B). The effect of various temperatures on compressive strength properties was assessed. The cubes were exposed to temperature ranging from 50 to 70 degrees C for a duration ranging from 2 to 10 h, and the compressive strength of the specimens was analyzed for destructive and non-destructive analysis and tested for 7, 28, and 90 days. The obtained compressive strength (CS) results were analyzed employing the probability plot (PP) curve, distribution overview curve (DOC), probability density function (PDF), Weibull, survival, and hazard function curve. Maximum compressive strength was achieved for the temperature of 70 degrees C and an A/B of 0.45 for destructive tests and non-destructive tests with 44.6 MPa and 43.56 MPa, respectively, on 90 days of testing. The survival and hazard function curves showed incremental distribution characteristics for 28 and 90 days of testing results with a probability factor ranging from 0.8 to 1.0. geopolymer concrete; compressive strength; alkaline to binder ratio; casting

Departments

Other Parts

Map

en.mapy.cz

Services

Popular Links

© 2023 University of Pardubice, Studentská 95, 532 10 Pardubice 2
Phone: +420 466 036 111, 466 036 112, 466 036 113
Webmaster, RSS
Data box ID: f5vj9hu
Accessibility Statement
CC BY-NC-ND 4.0