Formation of 2D-Structured InSe Ceramics from Amorphous Phase Deposited on a Kapton Foil
Authors: Svoboda Roman | Durčíková Lenka | Přikryl Jan | Hamano Keisuke | Fons Paul J | Krbal Miloš
Year: 2023
Type of publication: článek v odborném periodiku
Name of source: Journal of Physical Chemistry C
Publisher name: American Chemical Society
Place: Washington
Page from-to: 16132-16147
Titles:
Language Name Abstract Keywords
cze Tvorba 2D-strukturované InSe keramiky z amorfní fáze nanesené na Kaptonové pásce Kinetika tvorby 2D-vrstevnatých krystalů InSe ve amorfních vrstvách nanesených na Kaptonové pásce byla studována pomocí diferenciální skenovací kalorimetrie, ramanocvy spektroskopie, rentgenové difrakce a rentgenové absorpční spektroskopie. vrstevnaté InSe; krystalizační kinetika; Ramanova spektroskopie; DSC; růst
eng Formation of 2D-Structured InSe Ceramics from Amorphous Phase Deposited on a Kapton Foil The formation kinetics of the 2D-layered InSe crystallinephasein thin amorphous InSe films was studied by means of differentialscanning calorimetry, Raman spectroscopy, X-ray diffraction analysis,and X-ray absorption spectroscopy. All measurements were performedon as-deposited films (thicknesses ranging between 200 and 1500 nm),with Kapton foil used as a substrate. In the films with thickness & GE; 1000 nm, the formation was found to proceed via two steps:the exothermic re-organization of the amorphous phase (activationenergy of 420 kJ & BULL;mol(-1)), followed by the exothermicformation of the crystalline phase (activation energy of 227 kJ & BULL;mol(-1)). For InSe films with thickness & LE; 500 nm,the two processes merged, but their reaction mechanism was still foundto consist of two sequential phase transformations, with the reorganizationin the amorphous phase being the necessary preliminary step. Bothkinetic processes were found to be slowed down by the presence ofmechanical defects and by the surface/interface imperfections. Thepossibility of two-step preparation of ideally layered flexible 2DInSe ceramics is suggested based on the separated high-temperatureamorphous phase reorganization, followed by a low-temperature crystalgrowth step (during which excellent 2D InSe layering could be achieved). high-performance; multilayer inse; layered inse; crystallization kinetics; electronic-properties; raman-scattering; optical-response; ohmic contacts; growth; glass

Departments

Other Parts

Map

en.mapy.cz

Services

Popular Links

© 2023 University of Pardubice, Studentská 95, 532 10 Pardubice 2
Phone: +420 466 036 111, 466 036 112, 466 036 113
Webmaster, RSS
Data box ID: f5vj9hu
Accessibility Statement
CC BY-NC-ND 4.0Creative CommonsAttributionNonCommercialNoDerivatives