Crystal Growth in Se-Te Chalcogenides: Overview of the Growth/ Relaxation/Viscosity Interplay for Bulk Glasses and Thin Films
Authors: Svoboda Roman | Přikryl Jan | Provotorov Pavel | Kolobov Alexander V | Krbal Miloš
Year: 2023
Type of publication: článek v odborném periodiku
Name of source: Crystal Growth and Design
Publisher name: American Chemical Society
Place: Washington
Page from-to: 216−228
Titles:
Language Name Abstract Keywords
cze Krystalový růst Se-Te chalkogenidů: Přehled vzájemných vztahů mezi růstem, relaxací a viskozitou pro objemová skla a tenké filmy Kombinace mikroskopiské a kalorimetrické techniky byla použita pro studium krystalizačního chování tenkých vrstev Se-Te nanesených na kaptonové pásce, skle a křemenném skle. Nalezené chování bylo diskutováno s ohledem na chemické složení substrátu stejně jako relaxační a viskozitní chování Se-Te amorfní matrice. materiály s fázovou změnou; amorfní selen; strukturní relaxace; krystalizační kinetika; nukleace
eng Crystal Growth in Se-Te Chalcogenides: Overview of the Growth/ Relaxation/Viscosity Interplay for Bulk Glasses and Thin Films Crystal growth in 1 mu m Se(1-y)Tey thin films (for y = 0, 7, 10, and 17) deposited on the Kapton, SiO2 glass, and white glass substrates was researched and quantified by means of a unique combination of direct joint microscopic and calorimetric measurements. As a general feature, the crystal growth in the Se-Te thin films deposited on a Kapton tape was very close to the native/bulk crystal growth. Deposition on the inorganic glassy substrates largely accelerated the crystal growth in the Se-Te thin films due to the build-up of internal tension originating from the large difference in thermal expansion coefficients between the film and the substrate. An additional increase in the crystal growth rate was also caused by the diffusion of Na+ ions from the white glass substrate into the Se-Te films. Almost perfect correspondence was found for the activation energies of crystal growth determined by various measurement techniques (calorimetry and microscopy) and for various Se-Te sample forms (thin films, bulk glass, powdered bulk glass). A very good agreement was found also between the activation energies of viscous flow and structural relaxation at the glass transition temperature Tg. At higher temperatures, the Se-Te thin films exhibit a minor-to-moderate breach of the Stokes-Einstein law, as expressed by the value of Ediger's decoupling parameter xi approximate to 0.80 +/- 0.05. At lower temperatures near the glass transition, the violation of the Stokes-Einstein relation deepens for the thin films with higher Te content. An explanation was proposed based on the potential interconnection between the below-Tg relaxation kinetics and above-Tg connectivity of the undercooled liquid domains (resulting either in changes of the effective hydrodynamic radius during the self-diffusion or in the tendency to create structural inhomogeneities via thermal fluctuations). phase-change materials; amorphous selenium; structural relaxation; rearranging regions; optical-properties; crystallization; kinetics; temperature; transition; nucleation

Departments

Other Parts

Map

en.mapy.cz

Services

Popular Links

© 2023 University of Pardubice, Studentská 95, 532 10 Pardubice 2
Phone: +420 466 036 111, 466 036 112, 466 036 113
Webmaster, RSS
Data box ID: f5vj9hu
Accessibility Statement
CC BY-NC-ND 4.0Creative CommonsAttributionNonCommercialNoDerivatives