The influence of B2O3 on structure and ionic conductivity of lithium phosphate-niobate glasses
Authors: Hostinský Tomáš | Koudelka Ladislav | Mošner Petr | Tricot Gregory | Drobná Helena | Razum Marta | Santic Ana
Year: 2024
Type of publication: článek v odborném periodiku
Name of source: Journal of Non-Crystalline Solids
Publisher name: Elsevier Science BV
Place: Amsterdam
Page from-to: 123258
Titles:
Language Name Abstract Keywords
cze Vliv B2O3 na strukturu a iontovou vodivost fosfátových skel lithných modifikovaných oxidem niobičným Práce je zaměřena na studium vztahu mezi strukturou a vlastnostmi lithných niobáto-fosfátových skel modifikovaných přídavky oxidu boritého připravených v kompoziční řadě (100-x)[0.4Li2O-0.2Nb2O5-0.4P2O5]-xB2O3 s obsahem 0-48 mol% B2O3. borofosfátová skla; termické vlastnosti; struktura skla; NMR spektroskopie; Ramanova spektroskopie
eng The influence of B2O3 on structure and ionic conductivity of lithium phosphate-niobate glasses Glasses in the series (100-x)[0.4Li2O-0.2Nb2O5-0.4P2O5]-xB2O3 were prepared with B2O3 content ranging from 0 to 48 mol%. The glass transition temperature (Tg) increases with up to 8 mol% B2O3, peaking at 512 degrees C, then decreases to 490 degrees C at 40 mol% B2O3. Raman spectra at low B2O3 content indicate the presence of NbO6 octahedra. XRD patterns of crystallized samples reveal NbOPO4 formation across the entire composition range. Confrontation of the Raman spectra of glasses and crystalized glasses resulted in the assignment of the broad Raman band at 777-804 cm- 1 to Nb-O-Nb vibrations in the NbO6 octahedra. 11 B MAS NMR shows a transition from BO4 to BO3 units, while 31 P MAS NMR suggests mixed borate-phosphate structures. Using 2D NMR techniques, mixed species were identified in the glass network. Ionic conductivity remained stable up to 16 mol% B2O3 but decreased significantly at higher concentrations due to reduced Li+ ion mobility in the mixed phosphate-borate network. Borophosphate glasses; Thermal properties; Glass structure; NMR spectra; Raman spectra

Departments

Other Parts

Map

en.mapy.cz

Services

Popular Links

© 2023 University of Pardubice, Studentská 95, 532 10 Pardubice 2
Phone: +420 466 036 111, 466 036 112, 466 036 113
Webmaster, RSS
Data box ID: f5vj9hu
Accessibility Statement
CC BY-NC-ND 4.0