Subsolidus Area of the MgO-P2O5-Cr2O3 system: Synthesis, Properties and Application of Magnesium-chromium Phosphates as Colouring Substances
Authors: Błońska-Tabero Anna | Bosacka Monika | Filipek Elżbieta | Luxová Jana
Year: 2024
Type of publication: článek v odborném periodiku
Name of source: Journal of Thermal Analysis and Calorimetry
Publisher name: Springer
Place: Vídeň
Page from-to: 10465-10475
Titles:
Language Name Abstract Keywords
cze Subsolidusní oblast systému MgO-P2O5-Cr2O3: Syntéza, vlastnosti a aplikace hořčíko-chromových fosfátů jako barvících substancí Byly prozkoumány fázové vztahy v subsolidusní oblasti systému MgO-P2O5-Cr2O3. Reakce byly prováděny metodou vícestupňové kalcinace vzorků v teplotním rozmezí 350–1150 °C. Výsledkem provedeného výzkumu bylo objevení nového pyrofosfátu s chemickým vzorcem Mg5Cr2(P2O7)4. Tato sloučenina, krystalizující v ortorhombické soustavě, pravděpodobně vykazuje strukturu Fe5(2+)Fe2(3+)(P2O7)4. Bylo prezentováno infračervené spektrum nového pyrofosfátu. Mg5Cr2(P2O7)4 taje inkongruentně při 1330 °C a kdy vzniká Mg3Cr4(PO4)6. Vypracovaná dělení systému MgO-P2O5-Cr2O3 do podřízených subsystémů se výrazně liší od dříve známého z literatury. Především, na rozdíl od literatury, zohledňuje existenci právě objevené sloučeniny, stejně jako dalších dvou fosfátů, tj. Mg3Cr4(PO4)6 a Cr2P4O13. Tavení směsí fází, které koexistují v rovnovážném stavu, bylo odhadnuto pyrometrickou metodou. Všechny fosfáty (V) s mísenými kationty, tj. Mg5Cr2(P2O7)4, Mg3Cr4(PO4)6 a MgCr2(P2O7)2, byly testovány pro jejich použití pro barvení jednovýpalové bezolovnaté glazury vypalované při 1050 °C. Ukázalo se, že zkoumané fosfáty působí jako barvítka a byly získány keramické vrstvy dobré kvality a zajímavých barev. Optimální koncentrace aplikovaných fosfátů byla blízká 3 hmotnostním %. systém MgO-P2O5-Cr2O3;fázové rovnováhy;reakce v pevné fázi;fosforečnany chrom-hořečnaté;tepelná stabilita;barevné vlastnosti
eng Subsolidus Area of the MgO-P2O5-Cr2O3 system: Synthesis, Properties and Application of Magnesium-chromium Phosphates as Colouring Substances Phase relations in the subsolidus area of the MgO-P2O5-Cr2O3 system were reinvestigated. The reactions were carried out by the method of multi-stage calcination of samples in the temperature range of 350-1150 °C. As a result of the conducted research, a new pyrophosphate with the formula Mg5Cr2(P2O7)4 was discovered. This compound, crystallizing in the orthorhombic system, most likely exhibits the Fe5(2+)Fe2(3+)(P2O7)4 structure. The infrared spectrum of the new pyrophosphate was presented. Mg5Cr2(P2O7)4 melts incongruently at 1330 °C depositing Mg3Cr4(PO4)6. The developed division of the MgO-P2O5-Cr2O3 system into subsidiary subsystems differs significantly from the one known from the literature. First of all, unlike in the literature, it takes into account the existence of the compound just discovered, as well as the other two phosphates, i.e. Mg3Cr4(PO4)6 and Cr2P4O13. The melting points of mixtures of phases coexisting in the equilibrium state were estimated by the pyrometric method. All phosphates (V) with mixed cations, i.e. Mg5Cr2(P2O7)4, Mg3Cr4(PO4)6 and MgCr2(P2O7)2, were tested for their use for colouring lead-free glaze fired once at 1050 °C. It turned out that the investigated phosphates act as dyes and ceramic layers of good quality and interesting colours were obtained. The optimal concentration of the applying phosphates was close to 3 mass%. MgO-P2O5-Cr2O3 system;Phase equilibria;Solid state reactions;Chromium magnesium phosphates;Thermal stability;Colour properties

Departments

Other Parts

Map

en.mapy.cz

Services

Popular Links

© 2023 University of Pardubice, Studentská 95, 532 10 Pardubice 2
Phone: +420 466 036 111, 466 036 112, 466 036 113
Webmaster, RSS
Data box ID: f5vj9hu
Accessibility Statement
CC BY-NC-ND 4.0Creative CommonsAttributionNonCommercialNoDerivatives