SbxSe100-x system (0 < x < 8) studied by DSC and Raman spectroscopy.

Autoři: Holubová Jana | Černošek Zdeněk | Černošková Eva

Rok: 2007

Druh publikace: článek v odborném periodiku

Název zdroje: Optoelectronics and Advanced Materials - Rapid Communications

Název nakladatele: INOE & INFM Publishing House

Místo vydání: Bukurešť - Magurele

Strana od-do: 663-666

Tituly:

Jazyk	Název	Abstrakt	Klíčová slova
cze	Systém SbxSe100-x (0 < x < 8) studovaný pomocí DSC and Raman spektroskopie.	Skla systému SbxSe100-x (0 < x < 8) byla studována pomocí DSC and Raman spektroskopie.	DSC;Raman spektroskopie;krystalizace;Sb-Se systém
eng	SbxSe100-x system (0 < x < 8) studied by DSC and Raman spectroscopy.	The SbxSe100-x glass-forming system (x = 0, 1, 2, 4, and 8 at. %) was studied by conventional differential scanning calorimetry (DSC), Step Scan DSC and Raman spectroscopy. Glass transition temperature, Tg, as well as isobaric heat capacity change, ΔCp, were determined. Crystallization of Sb2Se3 from incongruent undercooled melt, followed by trigonal selenium crystallization was observed. The crystallization kinetics of Sb2Se3 was studied in details. Sb2Se3 crystallizes from incongruent melt at Tc = 107?2 oC with crystallization enthalpy ΔHc(Sb2Se3) = -52? J/g. Johnson-Mehl-Avrami kinetics of crystallization with Avrami kinetic exponent close to 3 was found.	DSC;StepScan DSC;Raman spectroscopy;selenium;Sb-Se system;glass transition;crystallization