Preparation and physical properties of luminescent 80GeSe(2) center dot (20-x)Sb2Se3 center dot xSb(2)Te(y):Pr2Se3 glasses; x=0, 1, 3, 10; y=2, 3, 4.

Autoři: Frumarová Božena | Frumar Miloslav | Oswald JIří | Kincl Miloslav | Parchanski Václav

Rok: 2013

Druh publikace: článek v odborném periodiku

Název zdroje: Journal of Luminescence

Název nakladatele: Elsevier Science BV

Místo vydání: Amsterdam

Strana od-do: 558-565

Tituly:

Jazyk	Název	Abstrakt	Klíčová slova
cze	Příprava a fyzikální vlastnosti luminiscenčních skel 80GeSe2(20-x)Sb2Se3xSb2Tey:Pr2Se3; x=0, 1, 3, 10; y=2,3,4.	Byla připravena skla systému 80GeSe(2) center dot (20-x)Sb2Se3 center dot xSb(2)Te(y):0.03Pr(2)Se(3) glasses; x=0, 1, 3, 10; y=2, 3, 4. Byla studována struktura a optické vlastnosti. Silná luminiscence byla naměřena ve spektrálních oblastech : 1100-1450nm,1500-1700nm,1750-2000,2000-2600nm a 3600-5200 nm.	chalkogenidová skla; MID IR luminiscence
eng	Preparation and physical properties of luminescent 80GeSe(2) center dot (20-x)Sb2Se3 center dot xSb(2)Te(y):Pr2Se3 glasses; x=0, 1, 3, 10; y=2, 3, 4.	Homogeneous glasses of the system 80GeSe(2) center dot (20-x)Sb2Se3 center dot xSb(2)Te(y):0.03Pr(2)Se(3) glasses; x=0, 1, 3, 10; y=2, 3, 4 were prepared. The glasses with x=0-3 are very stable without any crystallization for T < 600 degrees C. The T-g values (261-309 degrees C) and the E-g(opt) values (1.30-1.70 eV) are decreasing with the Te content. The index of refraction is high (2.55-2.73 for 2200 nm), it is increasing with increasing Te content. The Raman spectra revealed presence of GeSe4/2 tetrahedra, Ge2Se6/2 bi-tetrahedra and SbSe3/2 trigonal pyramids in studied glasses. The tellurium atoms are forming SbSe2Te and SbSeTe2 distorted pyramids. The strong luminescence corresponding to 4f transitions in Pr3+ ions was found in spectral regions (1100-1450 nm, 1500-1700 nm, 1750-2000, 2000-2600 nm and 3600-5200 nm; lambda(exc)=980, 1050 and 1550 nm). The intensities of luminescence bands depend on their composition.	chalcogenide glasses; MID IR luminescence