New concept of corrosion protection in the presence of water: V-active VCI. Concept and application

Autoři: Genovez Mario Celso | Araujo Luiz Henrique | Marques Dinis Pinto Tiago Alexandre | Hrdina Radim

Rok: 2015

Druh publikace: článek v odborném periodiku

Název zdroje: Anti-Corrosion Methods and Materials

Název nakladatele: Emerald Group Publishing Limited

Místo vydání: Bradford

Strana od-do: 53-58

Tituly:

Jazyk	Název	Abstrakt	Klíčová slova
cze	Nový koncept korozní ochrany v přítomnosti vody: V-active VCI. Koncept a aplikace	Účel - Práce popisuje výsledky zkoušek, jenž byly získány za použití nově vyvinutého typu organického inhibitoru: V-active VCI. Zjištění ukazují, že je možné odstranit nebo snížit oxidační působení vody, a tím se prodlužuje doby před lakováním po hydro tryskání, a že nová technologie inhibitoru koroze neinterferuje s kvalitou konečnou kvalitou přilnavosti barvy. Design/metodika/přístup - kovové vzorky byly ošetřeny/omyty pomocí hydrojetu (35.000 psi). Pak bylo použito vodného roztoku 2% V-active VCI SPH 1,712. Kovové destičky vzorků byly zkoumány po tryskání a po následném sušení a byly podrobeny zkouškám na přilnavost nátěru aby se vyhodnotila doba trvání dočasné ochrany a vliv na přilnavost nátěru. Nálezy - Použití navrhované V-active VCI technologie dovoluje minimalizovat nebo eliminovat oxidační působení vody, kdy je kov vystaven solné vlhkosti v uzavřeném prostředí, prodloužuje dobu před lakováním bez rušení v kvality konečného nátěru. Praktický dopad - Navržená technologie umožňuje zvětšit povrch očištěného ocelového plechu (připravený za mokra pískovaným), čímž se sníží náklady na pracovní sílu a cenu produktů a snižuje spotřebu vody. To má praktické aplikace při stavbě a údržbě lodí a produkci ropy a plynu. Také je vhodný k ochraně vnitřních povrchů potrubí, ochraně při hydrostatických testovacích procesech a čištění vody a proti korozi v naftových nádržích znečištěných vodou.	korozní ochrana; VCI; aplikace
eng	New concept of corrosion protection in the presence of water: V-active VCI. Concept and application	Purpose - This work describes test results that were obtained using a newly-developed type of organic inhibitor: V-active VCIs. The findings demonstrate that is possible to eliminate or reduce the oxidizing action of water, thereby extending the allowable time before painting after hydrojetting, and that the new corrosion inhibitor technology does not interfere with the final quality of paint adhesion. Design/methodology/approach - Metallic specimens were treated/washed by hydrojet (35000 Psi). It was employed as a 2 per cent V-active VCI SPH 1,712 water solution by dilution of the inhibitor in industrial water. Metal sample plates were examined after blasting and after subsequent drying, and were submitted to the paint adhesion tests, to evaluate the duration of temporary protection, oxidation prevention and influence on the adherence of paint (pull off). Findings - Using the V-active VCI proposed technology, it was possible to minimize or eliminate the oxidizing action of the water when the metal is exposed to the saline moisture in a closed environment, extending the acceptable time before painting without interference in the final quality of painting. Practical implications - The proposed technology allows to the area of prepared (wet blasted) steel surface to be increased during cleaning and preparation, thereby reducing labor and product costs, and reduces water consumption during the preparation process. Practical applications in the shipbuilding, ship maintenance and oil and gas production industries, include the preservation of internal tubes and pipes, protection during hydrostatic test processes and cleaning with water and corrosion prevention in diesel tanks contaminated with water.	Corrosion; Inhibitors; Oil and gas; Development; Green/environmental; VCI