The effect of Se a dagger" Te substitution on crystallisation micro-mechanisms evincing in GeTe4 glass

Autoři: Svoboda Roman | Brandová Daniela | Beneš Ludvík | Málek Jiří

Rok: 2016

Druh publikace: článek v odborném periodiku

Název zdroje: Journal of Thermal Analysis and Calorimetry

Název nakladatele: Springer

Místo vydání: Heidelberg

Strana od-do: 205-219

Tituly:

Jazyk	Název	Abstrakt	Klíčová slova
cze	Efekt substituce Se-Te na krystalizační mikromechanismy projevující se v GeTe4 skle	Izotermní a neizotermní krystalizační chování GeTe3,9Se0,1 chalkogenidového skla byl studován v závislosti na částicové velikosti a porovnáván s podobnou studií provedenou na čistém GeTe4 materiálu.	krystalizační kinetika; DSC; IČ mikroskopie; XRD; GeTe3,9Se0,1; Se-Te substituce
eng	The effect of Se a dagger" Te substitution on crystallisation micro-mechanisms evincing in GeTe4 glass	Isothermal and non-isothermal crystallisation behaviour of the GeTe3.9Se0.1 chalcogenide glass was studied dependent on particle size and compared to the similar DSC study performed for the pure GeTe4 material. The effect of the Se a dagger" Te substitution led to a decrease in the crystallisation process complexity in the case of powdered materials-the addition of Se led to domination of the slower nucleation-growth crystallisation mechanism over the fast autocatalytic growth from mechanically induced defects. The nature of the crystallisation mechanisms was confirmed by infrared microscopy and XRD. The addition of selenium into the GeTe4 matrix caused an enlargement of the identified crystallites; this, together with the overall deceleration of the crystallisation processes, indicates the suppression of nucleation processes. The presence of Se also greatly enhanced domination of the CNT-based three-dimensional growth of volume-located crystallites. The obtained findings provide a very good explanation for the markedly increased thermal stability of Se-doped Ge-Te infrared glasses.	Crystallisation kinetics; DSC; Infrared microscopy; XRD; GeTe3.9Se0.1; Se-Te substitution