Structure and properties of TeO2 containing lead phosphate glasses

Autoři: Mošner Petr | Koehler Sven | Vosejpková Kateřina | Koudelka Ladislav | Stachel Doerte

Rok: 2012

Druh publikace: článek v odborném periodiku

Název zdroje: Physics and Chemistry of Glasses: European Journal of Glass Science and Technology Part B

Název nakladatele: Society of Glass Technology

Místo vydání: Sheffield

Strana od-do: 45-51

Tituly:

Jazyk	Název	Abstrakt	Klíčová slova
cze	Struktura a vlastnosti olovnatých borofosfátových skel s obsahem TeO2	Byla studována struktura a vlastnosti olovnatých fosfátových skel s obsahem TeO2, připravených v kompozičních řadách (100 x)[0.5PbO-0.5P2O5]-xTeO2 (řada X) a 50PbO-(50-y)P2O5-yTeO2 (řada Y), kde x=0-80 mol% a y=0-25 mol% TeO2. S rostoucím obsahem TeO2 se zvyšuje teplotní roztažnost skel. Teplota skelné transformace a dilatační teplota měknutí vykazuje maximum u skel s obsahem x=50 mol% a y=25 mol% TeO2. Z DTA křivek vyplynulo, že všechna připravená skla, resp. jejich podchlazené taveniny krystalizují v teplotní rozmezí 380-550 C. Nejvyšší termická stabilita byla zjištěna u skel s obsahem 20-50mol%, u skel připravených v kompoziční řadě X. všechna připravená skla vykazují dobrou odolnost vůči působení vody. Z ramanových spekter vyplynulo, že s rostoucím obsahem TeO2 dochází k postupné depolymerizaci fosfátové strukturní sítě až na izolované tetraedrické jednotky Q(0).	fosfátová skla; telluričitá skla; struktura; vlastnosti
eng	Structure and properties of TeO2 containing lead phosphate glasses	Lead phosphate-tellurite glasses in the compositional series (100 x)[0.5PbO-0.5P(2)O(5)]-xTeO(2) (X-series) and 50PbO-(50-y)P2O5-yTeO(2) (Y-series) with x=0-80 mol% and y=0-25 mol% TeO2 were studied. The incorporation of TeO2 structural units into the lead metaphosphate glass results in a substantial decrease in their molar volume while the density increases in both compositional series. All prepared glasses exhibit good chemical durability against water corrosion. The additions of TeO2 to the starting 50PbO-50P(2)O(5) glass composition lead only to small changes of their thermal expansion coefficient within the range of 15.6-17.3 ppm degrees C-1. Glass transition temperature and dilatometric softening temperature reveal a maximum for the glass with x=50 mol% and y=25 mol% TeO2. DTA measurements showed that most of the glasses studied crystallise on heating in the temperature range of 380-550 degrees C. The lowest tendency towards crystallization was observed for the samples containing 20-50 mol% TeO2 in the compositional series (100-x)[0.5PbO-0.5P2O5]-xTeO2. Raman spectra indicated that the replacement of phosphate structural units by tellurite units is accompanied by the depolymerisation of phosphate chains and gradual transformation of Q(2) to Q(1) and Q(0) phosphate units.	phosphate glasses; tellurite glasses; structure; properties