The effect of material aging on crystallization kinetics of Se70Te30 glass

Autoři: Svoboda Roman | Málek Jiří | Podzemná Veronika

Rok: 2016

Druh publikace: článek v odborném periodiku

Název zdroje: Thermochimica Acta

Název nakladatele: Elsevier Science BV

Místo vydání: Amsterdam

Strana od-do: 25-34

Tituly:

Jazyk	Název	Abstrakt	Klíčová slova
cze	Efekt materiálového stárnutí na krystalizační kinetiku Se70Te30 skla	Efekt 6-ti měsíční degradace při pokojové teplotě na Se70Te30 krystalizační kinetiku byl testyován pomocí DSC v závislosti na experimentálních podmínkách jako jsou rychlost ohřevu a velikost částic. V případě velmi jemných částic, masivní degradace byla nalezena.	krystalizační kinetika; DSC; Se-Te sklo; dlouhodobá degradace
eng	The effect of material aging on crystallization kinetics of Se70Te30 glass	The effect of long-term room-temperature degradation (up to 6 months) on Se70Te30 crystallization kinetics was investigated by differential scanning calorimetry in dependence on experimental conditions of the measurement applied heating rate and particle size of the powdered material. In case of very fine powders massive amorphous-to-crystalline degradation occurred even at room temperature, indicating that the small powder grains have fully defects-imbued inner structure that accelerates crystal growth. The kinetic data obtained for the consequent crystallization of the remaining glassy matrix showed that the defects-based Johnson-Mehl-Avrami crystallization is under quasi-equilibrium conditions further accelerated towards autocatalytic mechanism. Coarse powders, on the other hand, exhibited primary degradation only in a surface layer of the powder grains. The main effect of the coarse powders aging was found to be associated with marked enhancement of crystal growth originating from volume-located nuclei-either a sub-T-g nucleation occurred during aging or some pre-existing nuclei were activated during this time (possibly via mechanical stresses arising from structural relaxation processes).	Crystallization kinetics; DSC; Se-Te chalcogenide glass; Long-term degradation

Vyhledávání

Přihlášení pro studenty

Přihlášení pro zaměstnance

Publikace detail

Katedry

Ústavy a pracoviště

Jak nás najdete?

Služby

Často hledáte