Crystallization kinetics in Se-Te glassy system-Effect of long-term material degradation

Autoři: Svoboda Roman

Rok: 2016

Druh publikace: článek v odborném periodiku

Název zdroje: Thermochimica Acta

Název nakladatele: Elsevier Science BV

Místo vydání: Amsterdam

Strana od-do: 108-119

Tituly:

Jazyk	Název	Abstrakt	Klíčová slova
cze	Krystalizační kinetika v Se-te systému - efekt dlouhodobé materiálové degradace	Vliv dlouhodobého skladování při pokojové teplotě na krystalizaci byl zkoumán pro sklovité vzorky Se90Te10, Se80Te20 a Se70Te30 pomocí metody DSC. Výsledky ukázaly rozsáhlý stupeň degradace vzniklý při skladování těchto materiálů při teplotách pod jejich teplotou skelné transformace.	krystalizační kinetika; DSC; Se-Te chalkogenidová skla; dlouhodobá degradace
eng	Crystallization kinetics in Se-Te glassy system-Effect of long-term material degradation	The influence of long-term laboratory-temperature degradation on the crystallization kinetics of the Se90Te10, Se80Te20 and Se70Te30 chalcogenide glasses was studied by differential scanning calorimetry. Periodical measurements during the 6 months aging period have shown that the fine Se-Te powders degraded largely, large degree of crystallinity occurred even though the materials were stored well below their glass transition temperature. The degradation increased with Te content. The defects-based residual crystallization kinetics exhibited by the fine Se-Te powders was not influenced significantly by the continuous degradation. Coarse Se-Te powders, on the other hand, exhibited only weak degradation with low amount of crystallinity occurring during the 6 months period but the crystallization kinetics of the degraded glasses changed markedly. The degraded coarse Se-Te powders have shown increased nuclei based volume-located growth of crystallites, which indicates that nucleation proceeded significantly below the glass transition; the effect increased largely with Te content.	Crystallization kinetics; DSC; Se-Te chalcogenide glass; Long-term degradation

Vyhledávání

Přihlášení pro studenty

Přihlášení pro zaměstnance

Publikace detail

Katedry

Ústavy a pracoviště

Jak nás najdete?

Služby

Často hledáte